The effect of annealing on thermostimulated processes of coloured sodium chloride crystals

Abstract

It is shown experimentally that after annealing samples of NaCl the thermoluminescence in the high-temperature maxima not only increases, which is in agreement with the results of other authors, but that simultaneously the thermoemission decreases. It follows from a discussion of the results that this effect is probably caused by the formation of a surface layer, which takes place during the evaporation of the sodium and both prevents the rise of the electrons from the crystal and the vacancies left in it by the sodium increase in the concentration of theV centres and thus the probability of luminescence.

Abstract

Экспериментально по казано, что после отжи га образцов NaCl не тольк о термо-люминесценци я в высокотемпературн ых максимумах возрас тает, но и одновременн о термоэмиссия уменьшается, Из обсуж дения результатов вы текает, что это явлени е вероятно вызвано поверхностн ым слоем, который возн икает в результате ис парения натрия и который с одной стор оны препятствует вых оду электронов из кри сталла, с другой стороны вакансии из-п од натрия, присутству ющие в нем, увеличиваю т концентрациюV-центров и тем самым в ероятность радиацио нной рекомбинации (лю минесценции).