Studies on tungstate gels

Summary

Ferric tungstate sols were prepared by the dialysis of the reaction products obtained after mixing varying amounts of 0.1 M sodium tungstate and 1.0 M ferric chloride. The sols on further dialysis gave gels. The times of setting of the gels were found to be dependent on the period of dialysis as well as on the ratio Wo₄−/Fe⁺⁺⁺. The variations in viscosity and conductivity were determined. It was found that the changes in viscosity were more pronounced than the conductance at the sol-gel transformation stage. The plots of the log time of setting against period of dialysis and the plots of log relative variations in viscosity and conductivity gave curves which in the major part were linear pointing towards the thixotropic nature of these gels. The variations in p_H under similar condition were found to be small.

Zusammenfassung

Ferriwolframat-Sole wurden durch Dialyse von Reaktionsprodukten präpariert, die nach Mischung verschiedener Mengen von 0,1 M Natrium wolframat und 1,0 M Ferrichlorid erhalten wurden. Die Sole ergaben bei weiterer Dialyse Gele. Die Absetzzeiten der Gele hängen sowohl von der Dauer der Dialyse als auch vom Verhältnis Wo₄/Fe⁺⁺⁺ ab. Die Änderungen in Viskosität und Leitfähigkeit wurden bestimmt. Die Änderungen der Viskosität sind ausgeprägter als die der Leitfähigkeit bei der Sol-Gel-Transformation. Log. Auftragungen der Absetzzeit gegen die Dauer der Dialyse und Auftragungen des Log. der relativen Änderungen von Viskosität und Leitfähigkeit ergaben Kurven, welche in dem größeren Teil linear sind und auf die thixotrope Natur dieser Gele hinweisen. Die Variationen im p_H unter gleichen Bedingungen wurden als gering festgestellt.