Mechanical resonance dispersion in polytetrafluorethylene rods in transverse vibration

Summary

Polytetrafluorethylene rods in transverse vibration exhibit sharp non-harmonic resonances when subjected to a static tensile stress during vibration. The extent and location of the resonances are critically dependent on the exact static stress state and history of the rods. Rods under no external tension have no anomalous behavior in the range 100 to 2000 cps, but under static tension varying from 1.5×10⁵ to 3.0×10⁶ dynes/cm² (2.2 to 44 psi) sharp resonances appear in the vicinity of 400 cps. The mechanical resonance dispersions in complex shear compliance previously reported byFitzgerald are thus substantiated by the present work. The failure of certain other investigators to observe the dispersion in polytetrafluorethylene is attributed to the fact that insufficient attention was paid to the static stress conditions in their tests.

Zusammenfassung

Polytetrafluoräthylen-Streifen zeigen bei transversaler Schwingung scharfe nicht-harmonische Resonanzen, wenn sie während der Vibration einem statischen Zug unterworfen sind. Intensität und Lage der Resonanzen hängen kritisch vom statischen Spannungszustand und der Geschichte der Proben ab. Proben unter keiner äußeren Spannung zeigen im Bereich von 100–200 Hz kein anomales Benehmen, doch erscheinen bei statischer Belastung zwischen 1,5×10⁵ zu 3,0×10⁶ dyn/cm² scharfe Resonanzen in der Nähe von 400 Hz. Die mechanische Resonanzdispersion der komplexen Scherungsnachgiebigkeit, früher vonFitzgerald mitgeteilt, werden mit der vorliegenden Arbeit bestätigt. Daß anderen Bearbeitern die Beobachtung der Dispersion bei Polytetrafluoräthylen mißlungen ist, ist der Tatsache zuzuschreiben, daß den statischen Spannungszuständen in ihren Proben ungenügende Rechnung zuteil wurde.