Studies on dielectric properties of polyacrylonitrile

Summary

The dielectric properties of polyacrylonitrile were measured over frequencies from 100 c/s to 2 Mc/s and temperatures from −70° C to 150° C, where only one dielectric absorption could be identified. In comparison with the result of visco-elastic measurement of polyacrylonitrile, it is concluded that the dielectric absorption will be attributed to the dipolar orientation related to the mierobrownian motion of segment.Cole andCole's circular arc law was satisfactorily applied to the data, andCole's parameter, (ε ₀−ε _∞) and$\bar \beta$ were determined at each temperature. (ε ₀−ε _∞) and$\bar \beta$ increase with the rise of temperature and reach to asymptotic values.

Zusammenfassung

Das dielektrische Verhalten von Polyacrylnitril wird über den Frequenzbereich von 100 Hz bis 2 MHz und für Temperaturen von −70° bis +150° C untersucht. Dabei konnte nur eine dielektrische Absorption festgestellt werden. Im Vergleich mit Ergebnissen viskoelastischer Messungen ist zu schließen, daß die dielektrische Absorption einer polaren Orientierung auf mikro-Brownscher Bewegung der Segmente beruht. DieColesche Darstellung läßt sich befriedigend auf die Messungen anwenden und die Parameter (ε ₀-ε _∞) und$\bar \beta$ für jede Temperatur lassen sich bestimmen. Beide Parameter steigen mit der Temperatur und erreichen asymptotische Werte.