Summary
A series of unfractionated and fractionated samples of polyvinyl acetate were prepared by homogeneous solution polymerization of vinyl acetate in N,N-dimethylformamide at 90 °C. in presence of γ, γ-azo-(γ-cyano-n-valeric acid) as initiator under a variety of conditions. A portion of each sample was hydrolysed to polyvinyl alcohol. The number average molecular weights have been determined by end-group titrations. The following molecular weight-intrinsic viscosity relationships for polyvinyl alcohol have been obtained. [η] = 33.88 X 10−5 M 0.716 — for unfractionated samples in water at 30 °C. [η] = 29.51 X 10−5 M 0.716 — for fractionated samples in water at 30 °C.
Similar content being viewed by others
References
Misra, G. S, V. P. Gupta, Makromol. Chem.71, 110 (1964).
Bamford, C. H., A. D. Jenkins, Nature176, 78 (1955).
Bamford, C. H., A. D. Jenkins, R. Johnston, Trans. Faraday Soc.55, 179 (1959).
Haines, R. M., W A. Waters, J. Chem. Soc. (London) 4256 (1955).
Schulz, G. V., G. Sing, J. Prakt. Chem.161, 161 (1943).
Matsumoto, M., Y. Ohyanagi, Kobunshi Kagaku (Chem. High Polymers, Tokyo),17,191 (1960).
Matsumoto, M., K. Imai, J. Polymer Sci.24, 125 (1957).
Matsuo, T., H. Inagaki, Makromol. Chem.55, 151 (1962).
Nakajima, A., K. Furutate, Kobunshi Kagaku (Chem. High Polymers, Tokyo)6, 460 (1949).
Author information
Authors and Affiliations
Additional information
With 1 figure and 2 tables
Rights and permissions
About this article
Cite this article
Misra, G.S., Mukherjee, P.K. The relation between the molecular weight and intrinsic viscosity of polyvinyl alcohol. Colloid & Polymer Sci 258, 152–155 (1980). https://doi.org/10.1007/BF01498273
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF01498273