Adsorption of stereoregular poly(vinyl alcohols) at air-water interface

Summary

The time dependency of the surface tension of the aqueous solutions of syndiotactic, isotactic and atactic poly(vinyl alcohols) (PVAs) for various concentrations were studied.

The rate of the decrease in the surface tension was highest for syndiotactic PVA and lowest for atactic PVA at the same concentration. The results were analysed as crystallization and diffusion processes. The rate is controlled by an intermolecular hydrogen bond formation of syndiotactic sequences at the surface for syndiotactic PVA and the easy arrangement of segments at the surface for isotactic and syndiotactic PVAs to influence the rate of diffusion of PVA molecules.

A filament could be made by picking up the multilayer formed at the surface of the syndiotactic PVA solution. The filament had the high orientation of PVA molecules and the similar properties as that from commercial PVA.

Zusammenfassung

Die Zeitabhängigkeit der Oberflächenspannung der wäßrigen Lösungen von syndiotaktischem, isotaktischem und ataktischem Poly(vinylalkohol) (PVA) wurde für verschiedene Konzentrationen untersucht.

Die Geschwindigkeit der zeitlichen Zunahme der Oberflächenspannung für das syndiotaktische PVA war die höchste und diejenige für ataktischen PVA die niedrigste. Die Ergebnisse wurden als Folge der Kristallisation und der Diffusionsprozesse gedeutet. Die Geschwindigkeit wird auf Grund einer zwischenmolekularen Wasserstoffbriickensbildung der syndiotaktischen Sequenzen bei syndiotaktischem PVA an die Oberfläche und mit der leichteren Einordnung der Segmente der isotaktischen und ataktischen PVA-Moleküle erklärt. Dies-beeinflußt die Diffusionsgeschwindigkeit der PVA-Moleküle entsprechend.

Man kann einen Faden dadurch spinnen, daß man die an die Oberfläche erzeugte Multischicht herauszupft. Das Filament hat die hohe Orientierung der PVA-Moleküle und ähnliche Eigenschaften wie die im Handel befindlichen PVAFasern.