Abstract
The emission of exoelectrons by metals after abrasion and after X-ray and neutron irradiation was investigated. The specimens were brought into a heatable counter. With a heating velocity of 2 °C/min the measured glow curves had peaks at 126 °C. This temperature depended only on the velocity of heating, but not on the metal (Al, Cu, Ag, Mo, Rh) or its purity and not on the quenching gas in the counter. To determine activation energies the measured glow curves are compared to calculated ones. There is strong evidence that nonmetallic layers are essential to exoelectron-emission from metals.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
Author information
Authors and Affiliations
Additional information
D 6. – Vgl. auch Eckey, H., Huster, E.: Z. Naturforsch.24a, 678 (1969).
Herrn Prof. Dr. E. Huster danke ich für die Anregung zu dieser Arbeit und sein stetes förderndes Interesse. Herrn Prof. Dr. H. Werner und Herrn Dr. G. Lamprecht, Institut für Numerische und Instrumentelle Mathematik und Rechenzentrum der Universität Münster, danke ich für ihre freundliche Unterstützung bei der Durchführung der Rechnungen. Die Arbeit wurde durch ein Stipendium der Stiftung Volkswagenwerk und durch Geldmittel des Landesamtes für Forschung in dankenswerter Weise gefördert.
Rights and permissions
About this article
Cite this article
Eckey, H. Temperaturverhalten der Exoelektronenemission von Metallen. Z. Physik 232, 87–100 (1970). https://doi.org/10.1007/BF01394947
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF01394947