The effect of the metallic additives (Al, Cr, and FeSi) on the properties of unfired periclase-carbon products was studied. It was shown that their presence decreases the degree of oxidation of graphite without decreasing the strength properties of the refractory. When heat treating the periclase-carbon specimens up to 1000°C, the effectiveness of the additives decreases in the following order: Al, Cr, FeSi. At 1400°C, the effectiveness of all the additives is virtually identical.
Similar content being viewed by others
Literature cited
I. G. Ochagova, Periclase-Carbon Products: Review Information (Ferrous Metallurgy. Ser. Refractories Industry) [in Russian], Inst. “Chermetinformatsiya,” Issue 1 (1985).
Toritani Hironobu, Kawakami Tatsuo, Tokahasi Hiroshi, et al., Ref. J.,36, No. 322, 629–635 (1984).
A. Jamaguchi, Refractories,35, No. 310, 3–8 (1983).
Author information
Authors and Affiliations
Additional information
Translated from Ogneupory, No. 8, pp. 7–9, August, 1989.
Rights and permissions
About this article
Cite this article
Kashcheev, I.D., Sizov, V.I. & Panin, O.A. Properties of periclase-carbon refractories containing metal powders. Refractories 30, 468–470 (1989). https://doi.org/10.1007/BF01280680
Issue Date:
DOI: https://doi.org/10.1007/BF01280680