Abstract
The present work deals with the occurrence of underclad cracks in three types of steels differing in the contents of the alloying elements (Cr, Ni, Mn) and in the impurities level (As, Sb, Sn). The presence of the intercrystalline fracture typical for the underclad cracks was proved to be dependent on the temperature and on the ageing time. It follows from the results of Auger electron spectroscopy, that the sulphur and phosphorus segregations accompanied by a higher number of carbide (possibly sulphide) particles cause a decrease of grain boundary strength. Segregations of other impurity elements were not detected at grain boundaries.
Similar content being viewed by others
References
A. G. Vinckier, A. W. Pense,WRC Bull. 1974, 197.
R. E. Dolby, G. C. Saunders,Met. Const. 1978,12, 20.
G. Wellnitz, E. Schmidtmann,Proc. of 2nd Roll. Schweißen in der Kerntechnik, Düsseldorf, 1974, p. 321.
K. Kussmaul, J. Ewald, G. Maier,Schweißen und Schneiden 1976,28, 219.
P. Auger,Surf. Sc. 1975,48, 1.
L. E. Davis, N. C. McDonald, P. W. Palmberg, G. E. Riach, R. E. Weber,Handbook of AES, PHI, Eden Prairie, Minnesota, 1976.
A. Dhooge, A. Vinckier, A. W. Pense,Int. J. Press. Ves. Piping 1978,6, 329.
K. Kussmaul, K. Hem, K. Tham, W. Dietrich, D. Huppler,Proc. of 5th Int. Conf. on Strength of Metals and Alloys, Aachen, 1979, p. 1455.
H. Horn, H. D. Kunze,Proc. of 4th Int. Koll. Schweißen in der Kerntechnik, Aachen, 1982, p. 276.
A. S. Zubčenko, M. M. Timofjejev, A. V. Fedorov,Svar. Proizv. 1976, 39 (in Russian).
R. Z. Šron, L. E. Krečet, V. A. Ignatov, E. A. Suslova,Avtom. Svarka 1980, 11 (in Russian).
M. P. Seah,J. Microsc. Spectr. Electr. 1983,8, 177.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Koutník, M., Landa, V. AES study of underclad cracking. Mikrochim Acta 91, 429–435 (1987). https://doi.org/10.1007/BF01199518
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF01199518