Abstract
For a commercial Mg-Al-Zn alloy sheet, tensile tests are carried out under various strains, strain rates and temperatures to investigate the possibility of grain refinement by dynamic recrystallization during pre-deformation. It is found from the microstructural observations that relatively fine grains of 10 μm or so, in diameter are attained under the conditions of 250°C and 8.3 × 10−4 s−1. The specimen pre-strained under this condition also exhibits a fairly good superplasticity of total elongation beyond 300%.
Similar content being viewed by others
References
R. GGrimes, M. J. Stowell andB. M. Watts,Met. Technol. 3 (1976) 154.
B. M. Watts, MM. J. Stowell, B. L. Baikie andD. G. E. Owen,Met. Sci. 10 (1976) 189.
J. A. Wert, N. E. Paton, C. H. Hamilton andM. W. Mahoney,Met. Trans. 12A (1981) 1267.
N. E. Paton, C. H. Hamilton, J. Wert andM. Mahoney,J. Met. 34 (1982) 21.
A. J. Shakesheff andP. G. Partridge,J. Mater. Sei. 20 (1985) 2408.
H. Takuda, S. Kikuchi andN. Hatta, J. Mater. Sci., in press.
J. Wadsworth, A. R. Pelton andR. E. Lewis,Met. Trans. 16A (1985) 2319.
A. J. Shakesheff andP. G. Partridge,J. Mater. Sci. 21 (1986) 1368.
D. Lee andW. A. Backofen,Trans. AIME. 239 (1967) 1034.
N. E. Paton andC. H. Hamilton,Met. Trans. 10A (1979) 241.
W. A. Backofen, G. S. Murty andS. W. Zehr,Trans. AIME. 242 (1968) 329.
M. M. Tilman andL. A. Neumeier, Bureau of Mines Report of Investigations RI8662 (1982).
R. Z. Valiev andO. A. Kaibyshev,Phys. Stat. Sol. 44 (1977) 477.
G. Piatti andT. Stoto,J. Mater. Sei. Lett. 3 (1984) 60.
A. W. Thompson,Metallogr. 5 (1972) 366.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Takuda, H., Kikuchi, S. & Hatta, N. Possibility of grain refinement for superplasticity of a Mg-AI-Zn alloy by pre-deformation. J Mater Sci 27, 937–940 (1992). https://doi.org/10.1007/BF01197645
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01197645