The effect of atmosphere control on the sintering behaviour of TiB2-20 wt% Ni ceramics was investigated. Sintering was performed at 1700 °C for 1h with commercial TiB2 powders produced by the earbothermic reaction. Under a fixed single atmosphere such as vacuum or Ar, densification was limited and large pores remained. However, a sintered density above 99% of theoretical could be achieved by a two-step sintering procedure in which the atmosphere was changed from vacuum to Ar at 1600 °C during the heat-up with subsequent isothermal sintering being performed at 1700 °C for 1h. Qualitative considerations about these phenomena are discussed.
Similar content being viewed by others
References
J. Castaing andP. Costa, in “Boron and Refractory Borides”, edited by V. I. Matkovich (Springer-Verlag, New York, 1977) p. 390.
M. L. Wilkins,ibid.in “) p. 633.
V. J. Tennery, C. B. Finch, C. S. Yust andG. W. Clark, in “Science of Hard Materials”, edited by R. K. Viswanadham, D. J. Rowcliffe and J. Gurland (Plenum Press, New York, 1983) p. 891.
E. V. Clougherty, R. L. Pober andL. Kaufman, in “Modern Developments in Powder Metallurgy, Vol. 2”, edited by H. H. Hausner (Plenum Press, New York, 1966) p. 891.
D. Kalish andE. V. Clougherty,Amer. Ceram. Soc. Bull. 48 (1969) 570.
M. K. Ferber, P. F. Becher andC. B. Finch,J. Amer. Ceram. Soc. 66 (1983) C-2.
H. R. Baumgartner andR. A. Steiger,ibid. 67 (1984) 207.
C. B. Finch, P. F. Becher, P. Angelini, S. Baik, C. E. Bamberger andJ. Brynestad,Adv. Ceram. Mater. 1 (1986) 50.
E. S. Kang, C. W. Jang, C. H. Lee, C. H. Kim andD. K. Kim,J. Amer. Ceram. Soc. 72 (1989) 1868.
S. Baik andP. F. Becher,ibid. 70 (1987) 527.
B. Yu Yuriditskii, V. A. Pesin andS. S. Ordan'yan,Poroshk. Metall. 4 (1982) 32.
S. S. Ordan'yan, B. Yu Yuriditskii andI. B. Panteleev,ibid. 7 (1982) 94.
K. Nishiyama andS. Umekawa, in “Composites '86: Recent Advances in Japan and the United States”, (Proc. Japan-U.S. CCM-III, Tokyo, Japan, 1986) edited by S. Umekawa and A. Kobayashi, p. 433.
T. K. Gupta andR. L. Coble,J. Amer. Ceram. Soc. 51 (1968) 525.
C. S. Morgan, K. H. Mccorkle andG. L. Powell,ibid. 59 (1976) 104.
R. M. German andK. S. Churn,Metall. Trans. A 15A (1984) 747.
S. J. Cho, S. J. L. Kang andD. N. Yoon,ibid. 17A (1986) 2175.
J. J. Kim, B. K. Kim, B. M. Song, D. Y. Kim andD. N. Yoon,J. Amer. Ceram. Soc. 70 (1987) 734.
U. C. Oh, Y. S. Chung, D. Y. Kim andD. N. Yoon,ibid. 71 (1988) 854.
O. J. Kwon andD. N. Yoon, in “Sintering Processes”, edited by G. C. Kuczynski (Plenum Press, New York, 1980) p. 203.
H. H. Park, S. J. Cho andD. N. Yoon,Metall. Trans. A 15A (1984) 1075.
Y. Masuda andR. Watanabe, in “Sintering Processes”, edited by G. C. Kuczynski (Plenum Press, New York, 1980) p. 3.
C. Greskovich,J. Amer. Ceram. Soc. 64 (1981) 725.
P. S. Sklad andC. S. Yust, in “Science of Hard Materials”, edited by R. K. Viswanadham, D. J. Rowcliffe and J. Gurland (Plenum Press, New York, 1983) p. 911.
T. M. Shaw,J. Amer. Ceram. Soc. 69 (1986) 27.
D. N. Yoon andW. J. Huppmann,Acta Metall. 27 (1979) 693.
S. J. L. Kang, K. H. Kim andD. N. Yoon,J. Amer. Ceram. Soc. 74 (1991) 425.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Kim, WJ., Kim, DH., Kang, E.S. et al. Two-step sintering of a TiB2-Ni cermet. J Mater Sci 31, 5805–5809 (1996). https://doi.org/10.1007/BF01160832
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01160832