Abstract
Phases in equilibrium with the αZr solid solution from 1014–1314 °C (1287–1587 K) in zirconium-tin-oxygen alloys were characterized and their compositions were determined. The experimental results provide information on the equilibria of the αZr solid solution in order to propose tentative boundaries at isothermal sections of the phase diagram.
Similar content being viewed by others
References
D. Arias andL. Roberti,J. Nucl. Mater. 118 (1983) 143.
L. Roberti, Doctoral Thesis, Universidad Nacional de Buenos Aires (1992) p. 89.
Y.-U. Kwon andJ. Corbett,Chem. Mater. 4 (1992) 187.
T. Tsuji, M. Amaya andK. Naito,J. Nucl. Mater. 201 (1993) 126.
J. Stöcker andR. Collongues,Compt. Rend. 244 (1957) 83.
J. Collins andI. Ferguson,J. Chem. Soc. (A) (1968) 4.
G. Wilson andF. Glasser,Trans. Br. Ceram. Soc. 88 (1989) 69.
J. Abriata, J. Garcés andR. Versaci,Bull. Alloy Phase Diag. 7 (1986) 116.
J. Abriata, J. Bolcich andD. Arias,ibid. 4 (1983) 147.
J-P. Langeron, “Oxides de Zirconium” in “Nouveau Traité de Chimie Minérale”, P. Pascal (ed), Vol. IX (Masson, Paris, 1963) p. 485.
J. Betterton Jr andD. Easton,J. Metals 13 (1961) 86.
B. O. Lichter,Trans. Metall. Soc. AIME 218 (1960) 1015.
Y.-U. Kwon andJ. D. Corbett,Chem. Mater. 2 (1990) 27.
G. Gran andS. Andersson,Acta Chem. Scand. 14 (1960) 956.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Aricó, S.F., Gribaudo, L.M. & Roberti, L.A. Equilibrium phases surrounding the αZr solid solution in the Zr-Sn-O system. J Mater Sci 31, 5587–5591 (1996). https://doi.org/10.1007/BF01160802
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01160802