Abstract
A variety of inorganic aluminium sols were investigated for their reactivity with colloidal silica to form polycrystalline mullite. Nuclear magnetic resonance (NMR) spectroscopy was used on the precursor aluminium sols to ascertain the co-ordination and reactivity of the species present. Differential thermal and thermogravimetric analysis and X-ray diffraction were used to analyse the products of the fired xerogels. Commercial reactants produced diphasic materials with little or no mullite formed at 1000 °C. A monomeric/dimeric sol produced in house however, showed a sharp exotherm at 920 °C and crystalline mullite formation at this temperature.
Similar content being viewed by others
References
D. W. Hoffman andR. Roy,J Amer Ceram Soc 67 (1984) 468.
A. K. Chakravorty andD. K. Ghosh,ibid 69 (1986) C-202.
E. B. Yoldas andD. P. Partlow J Mater Sci 23 (1988) 895.
C. S. Hsi, H. Y. Lu andF. S. Yen,J Amer Ceram Soc 72 (1989) 2208.
A. K. Bhattacharya, A. Hartridge andK. K. Mallick,J Mater Sci 31 (1996) 267.
Idem, ibid (1996) (in press).
M. J. Hyatt andN. P. Bausal,ibid 25 (1990) 2815.
M. Mizuno andH. Saito,J Amer Ceram Soc 72 (1989) 377.
M. G. M. U. Ismail, Z. Nakai andS. Somiya,ibid 70 (1987) C-7.
M. G. M. U. Ismail, H. Tsunatori andZ. Nakai,ibid 73 (1990) 537.
A. Taylor andD. Holland,J Non-Cryst Solids. 152 (1993) 1.
D. Taylor,ICI, internal communication.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Bhattacharya, A.K., Hartridge, A. & Mallick, K.K. Inorganic aluminium precursors in the synthesis of mullite — an investigation. J Mater Sci 31, 5551–5554 (1996). https://doi.org/10.1007/BF01159329
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01159329