Literature cited
M. A. Krishtal and B. M. Drapkin, “A unit for simultaneous determination of the moduli of elasticity and shear, and the decrement of oscillations over a vide temperature range,” Zavod. Lab.,31, No. 11, 1391–1393 (1965).
G. Schoeck, “Friction interna debido a la interaction entre dislocaciones y atomas solutos,” Acta Met.,11, No. 6, 617–622 (1967).
V. I. Sarrak and S. O. Suvorova, “The 200° maximum of internal friction and residual microstresses in martensite,” Dokl. Akad. Nauk SSSR,208, No. 2, 338–341 (1975).
M. A. Krishtal, Ya. I. Yarkhin, L. E. Épshtein, and N. N. Sergeev, “The influence of the level of stresses on hydrogen corrosion of steel reinforcement,” Metalloved. Term. Obrab. Met., No. 5, 59–63 (1973).
S. S. Nosyreva, “The influence of structure on the diffusion of hydrogen in steel,” Stal',8, No. 6, 542–545 (1948).
S. S. Gorelik, L. N. Rastorguev, and Yu. A. Skakov, X-Ray Diffraction and Electron Diffraction Analysis of Metals [in Russian], Metallurgiya, Moscow (1970).
N. N. Sergeev and V. S. Ageev, “The change in physicomechanical properties of 20GS2 reinforcing steel in long-term strength tests in a hydrogen-containing medium,” in: Questions of Physical Metallurgy and Metal Physics [in Russian], Tula (1977), pp. 110–117.
Author information
Authors and Affiliations
Additional information
Translated from Fiziko-Khimicheskaya Mekhanika Materialov, Vol. 17, No. 1, pp. 20–23, January–February, 1981.
Rights and permissions
About this article
Cite this article
Sergeev, N.N., Ageev, V.S. & Belobragin, Y.A. Hydrogen embrittlement of 20GS2 reinforcing steel in long-term strength tests. Mater Sci 17, 17–20 (1981). https://doi.org/10.1007/BF01156720