Abstract
Bi(Al)-Ca-Sr Cu-O glass-ceramic fibres over 100 cm in length were successfully drawn from a glass preform above the crystallization temperature,T x. The diameters of the uniformly drawn fibres with circular cross-section could be controlled in the range from 25–200 μm and the drawing speed was as high as 200 cm min−1. In this work Al2O3 was used to modify the properties of the glass. It increased the glass transition and crystallization temperatures but did not significantly increase the glass working range. Shrinkage and increase of density during heat treatment of the glass fibres were observed. The annealed (825°C/12 h in air) Bi4Al0.1Ca3Sr3Cu4Oy glass-ceramic fibre showed aT c(onset) of 82 K and aT c(zero) of 71 K.
Similar content being viewed by others
References
G. F. Delafuente, R. Navarro, F. Lera andC. Rillo,J. Mater. Res. 6 (1991) 699.
A. Kurosaka, M. Aoyagi, H. Tominaga, O. Fukuda andH. Osanai,Appl. Phys. Lett. 55 (1989) 390.
S. Katayama andM. Sekine,J. Mater. Res. 6 (1991) 1629.
M. Onishi, T. Kohgo, Y. Chigusa, K. Watanabe, M. Kyoto andM. Watanabe,Jpn J. Appl. Phys. 29 (1990) L64-L66.
T. Komatsu, C. Hirose, T. Ohki, R. Sato andK. Matusita,Appl. Phys. Lett. 57 (1990) 183.
H. Zheng andJ. D. Mackenzie,Phys. Rev. B 38 (1989) 7166.
T. Kanai, T. Kumagai, A. Soeta, T. Suzuki, K. Aihara, T. Kamo andS. Matsuda,Jpn J. Appl. Phys. 27 (1988) L1435.
N. Tohge, S. Tsuboi, Y. Akamatsu, M. Tatsumisago andT. Minami,Nippon Seramikkusu Kyokai Ronbunshi 97 (1989) 334.
R. Xu, H. Zheng andJ. D. Mackenzie, in “Superconductivity and Ceramic Superconductors”, edited by K. M. Nair and E. A. Giess (American Ceramic Society, Westerville, OH, 1990) pp. 653–67.
H. Zheng, M. W. Colby andJ. D. Mackenzie,J. Non-Cryst. Sol. 27 (1991) 143.
H. Zheng andJ. D. Mackenzie,Phys. Rev. B 43 (1991) 3048.
D. C. Tran, R. J. Ginther andG. H. Sigel Jr,Mater. Res. Bull. 17 (1982) 1177.
H. Zheng andJ. D. Mackenzie, in “Proceedings of the XV International Congress on Glass”, USSR, 1989, to be published.
H. Zheng, R. Xu andJ. D. Mackenzie,J. Mater. Res. 4 (1989) 911.
H. Zheng, Y. Hu andJ. D. Mackenzie,Appl. Phys. Lett. 58 (1991) 1679.
H. W. Schneider, A. Schoberth andA. Standt,Glastech. Ber. 60 (1987) 205.
C. W. Chu, J. Bechtold, L. Gao, P. H. Hor, Z. J. Huang, R. L. Meng, Y. Y. Sun, Y. Q. Wang andY. Y. Xue,Phys. Rev. Lett. 60 (1988) 941.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Hu, Y., Zheng, H. & Mackenzie, J.D. High-T c superconducting Bi(Al)-Ca-Sr-Cu-O glass-ceramic fibres drawn from glass preforms. J Mater Sci 30, 3913–3918 (1995). https://doi.org/10.1007/BF01153956
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01153956