Abstract
Ceramics of zirconium titanate, ZrTiO4, were prepared by the mixed oxide route, sintered at 1400 °C and cooled at various rates: water quench to 1 °C h−1. Mixed oxide-prepared ceramics of Zr5Ti7O24 were sintered at 1400 °C and cooled at 6 °C h−1. TEM analysis of the ZrTiO4 ceramics showed the development of an incommensurate superstructure in the more slowly cooled specimens. The Zr5Ti7O24 ceramics exhibited a commensurate superstructure with a tripleda-axis. Raman spectra were obtained from polished ceramic specimens at room temperature. Major differences between spectra for ZrTiO4 ceramics are believed to reflect differences in the degree of cation ordering. The Raman spectrum for Zr5Ti7O24 is similar to that of slowly cooled ZrTiO4 but there are significant differences.
Similar content being viewed by others
References
F. Azough andR. Freer, in “Proceedings of the 7th IEEE Symposium on Applications of Ferroelectrics”, June 1990, University of Illinois at Urbana-Champaign, USA (IEEE, Piscataway NJ, 1991) pp. 198–201.
K. Wakino, K. Minai andH. Tamura,J. Amer. Ceram. Soc. 67 (1984) 278.
U. S. Pat. 4665 041 (1987).
K. Wakino, in “Proceedings of the 6th IEEE International Symposium on Applications of Ferroelectrics”, June 1986, Bethlehem, PA (IEEE, Piscataway NJ, 1986) pp. 97–106.
R. E. Newnham,J. Amer. Ceram. Soc. 50 (1967) 216.
A. E. McHale andR. S. Roth,ibid. 66 (1983) C-18.
F. Azough, PhD thesis, University of Manchester (1991).
H. Tamura, D. A. Sagala andK. Wakino,Jp. J. Appl. Phys. 25 (1986) 787.
J. Petzelt, S. Pacesova, J. Fousek, S. Kamba, V. Zelezny, V. Koukal, J. Schwarzbach, B. P. Gorshumov, G. V. Kozlov andA. A. Volkov,Ferroelectrics 93 (1989) 77.
M. A. Krebs andR. A. Condrate,J. Mater. Sci. Lett. 7 (1988) 1327.
A. E. McHale andR. S. Roth,J. Amer. Ceram. Soc. 69 (1986) 827.
P. Bordet, A. McHale, A. Santoro andR. S. Roth,J. Solid. State Chem. 64 (1986) 30.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Azough, F., Freer, R. & Petzelt, J. A Raman spectral characterization of ceramics in the system ZrO2-TiO2 . J Mater Sci 28, 2273–2276 (1993). https://doi.org/10.1007/BF01151652
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01151652