An adsorbed monolayer of the organic inhibitor nitrilotris methylene phosphonic acid (NTMP) improves the bond durability of 2024 aluminium adherends prepared by phosphoric acid anodization (PAA). As had previously been determined for Forest Products Laboratories (FPL)-prepared adherends, maximum improvements occurred when a monolayer of NTMP was adsorbed onto the surface. Examination of the wedge test failure surfaces of PAA adherends treated in NTMP revealed that although crack propagation had initially involved oxide to hydroxide conversion of the original PAA oxide, the locus of failure transfers to the adhesive near the surface quite early in the test. This means that the failure of NTMP-treated PAA adherends was predominantly cohesive through the adhesive.
Similar content being viewed by others
References
J. D. Venables, D. K. McNamara, J. M. Chen, T. S. Sun andR. L. Hopping,Appl. Surf. Sci. 3 (1979) 88.
J. D. Venables, D. K. McNamara, J. M. Chen, B. M. Ditchek, T. I. Morgenthaler andT. S. Sun, Proceedings of the 12th National SAMPE Technical Conference (SAMPE, Azusa, California, 1980) p. 909.
D. A. Vermilyea andW. Vedder,Trans. Faraday Soc. 66 (1970) 2644.
G. D. Davis, T. S. Sun, J. S. Ahearn andJ. D. Venables,J. Mater Sci. 17 (1982) 1809.
J. S. Ahearn, G. D. Davis, T. S. Sun andJ. D. Venables, in “Adhesion Aspects of Polymer Coatings”, edited by K. Mittal (Plenum Press, New York) p. 281.
D. A. Hardwick,J. S. Ahearn,andJ. D. Venables,J. Mater Sci. 19 (1984) 223.
D. Broek, “Elementary Engineering Fracture Mechanics” (Sijthoff and Noordhoff, Alphen aan den Rijn, Netherlands, 1978) p. 154.
M. H. Stone andT. Peet, Royal Aircraft Establishment, Technical Memo MAT 349, July, 1980.
T. S. Sun,D. K. McNamara,J. S. Ahearn, J. M. Chen, B. Ditchek andJ. D. Venables,Appl. Surf. Sci. 5 (1980) 406.
J. S. Ahearn, T. S. Sun, C. Froede andJ. D. Venables, in Proceedings of ASM/SAMPE Conference on Specialized Cleaning Finishing and Coating Processes (Los Angeles, CA, 1980) alsoSAMPE Quarterly 12 (1980) 39.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Hardwick, D.A., Ahearn, J.S., Desai, A. et al. Environmental durability of phosphoric acid anodized aluminium adhesive joints protected with hydration inhibitors. J Mater Sci 21, 179–187 (1986). https://doi.org/10.1007/BF01144718
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01144718