Abstract
TiC x and VC x have wide non-stoichiometric composition ranges which come only from the carbon vacancies. High purity single crystals with controlled compositions were prepared, and their electrical resistivities at 4.2 and 298 K were measured as a function of composition. In the case of TiC x whose carbon vacancies are disordered in the lattice, the dependence of the residual resistivity on the composition was interpreted' by applying Nordheim's rule to the vacancy scattering and by considering the change in carrier density due to the introduction of vacancies. In addition, the difference in the resistivity between 4.2 and 298 K was discussed. In the case of VC x whose carbon vacancies are ordered, the dependence of the resistivity on the composition ranges of the ordered phases was examined in detail.
Similar content being viewed by others
References
L. E. Toth, in “Transition Metal Carbides and Nitrides” (Academic Press, New York, 1971) p. 4.
M. Aono, Y. Hou, R. Souda, C. Oshima, S. Otani andY. Ishizawa,Phys. Rev. Lett. 50 (1983) 1293.
C. Oshima, R. Souda, M. Aono, S. Otani andY. Ishizawa,Phys. Rev. 30 (1984) 5361.
R. Souda, M. Aono, C. Oshima, S. Otani andY. Ishizawa,Surf. Sci. 150 (1985) L59.
Y. Ishizawa andT. Tanaka,Solid State Commun. 51 (1984) 743.
S. Otani, T. Tanaka andY. Ishizawa,J. Cryst. Growth 61 (1983) 1.
Y. Hou, S. Otani, T. Tanaka andY. Ishizawa,ibid. 68 (1984) 733.
S. Otani, T. Tanaka andY. Ishizawa,ibid. 71 (1985) 615.
N. F. Mott andH. Jones, in “The Theory of the Properties of Metals and Alloys” (Dover Publication, New York, 1958) p. 296.
B. M. Klein, D. A. Papaconstantopoulos andL. L. Boyer,Phys. Rev. B22 (1980) 1946.
W. S. Williams,Phys. Rev. 135 (1964) A505.
Idem, “Progress in Solid State Chemistry”, Vol. 6 (Pergamon Press, Oxford, 1971) p. 57.
H. Ihara, Y. Kumashiro andA. Itoh,Phys. Rev. B12 (1975) 5465.
L. W. Shacklette andW. S. Williams,ibid. B7 (1973) 5041.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Otani, S., Tanaka, T. & Ishizawa, Y. Electrical resistivities in single crystals of TiC x and VC x . J Mater Sci 21, 1011–1014 (1986). https://doi.org/10.1007/BF01117387
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01117387