Abstract
The hardness and indentation damage of chemical vapour-deposited SiC coating/graphite substrate composites have been studied. Experimental results indicate that hardness is a non-linear function of coating thickness, and is not significantly affected by the changes in the magnitude of the residual stresses in SiC coating. The size of indentation lateral crack, observed using optical microscopy, varies with coating thickness. Acoustic emission spectra show that thinner coatings suffer more extensive fracture as compared with thicker coatings.
Similar content being viewed by others
References
B. R. Lawn andE. R. Fuller,J. Mater. Sci. 19 (1984) 4061.
M. F. Gruninger, B. R. Lawn andE. N. Farabaugh,J. Amer. Ceram. Soc. 70 (1987) 344.
K. Kamata, N. Aizawa andM. Moriyama,J. Mater. Sci. Lett. 5 (1986) 1055.
P. H. Kobrin andA. B. Harker,J. Mater. Sci. 24 (1989) 1363.
R. B. King,Int. J. Solids Struct. 23 (1987) 1657.
A. G. Evans andJ. W. Hutchinson,ibid. 20 (1984) 455.
C. Rossington, A. G. Evans, D. B. Marshall andB. T. K. Yakub,J. Appl. Phys. 56 (1984) 2639.
J. E. Ritter, T. J. Lardner, L. G. Rosenfeld andM. R. Lin,ibid. 66 (1989) 3626.
L. G. Rosenfeld, J. E. Ritter, T. J. Lardner andM. R. Lin,ibid. 67 (1990) 3291.
V. R. Howes andM. A. Ryan,J. Austral. Ceram. Soc. 22 (1986) 13.
A. K. Bhattacharya andW. D. Nix,Int. J. Solids Struct. 24 (1988) 1287.
B. Jonsson andS. Hogm Ark,Thin Solid Films 114 (1984) 257.
G. R. Anstis, P. Chantikul, B. R. Lawn andD. B. Marshall,J. Amer. Ceram. Soc. 64 (1981) 533.
C. C. Chiu,ibid 64 (1990) 1999.
R. D. Rawlings, in “Surface Coatings-2” (Elsevier Applied Science, New York, 1988) p. 71.
B. R. Lawn andM. V. Swain,J. Mater. Sci. 10 (1975) 113.
R. B. King andT. C. O'sullivan,Int. J. Solids Struct. 23 (1987) 581.
P. K. Gupta andJ. A. Walowit,Trans ASME, J. Lub. Tech. 96 (1974) 250.
W. T. Chen andP. A. Engel,Int. J. Solids Struct. 8 (1972) 1257.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Chiu, CC. Hardness and indentation-induced damage of SiC-coated graphite. J Mater Sci 27, 3353–3358 (1992). https://doi.org/10.1007/BF01116036
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01116036