Abstract
The boron-containing hard-type (HT) carbons were prepared by heating the raw coke compacts with 1.6 wt% boron at temperatures ranging from 1000 to 2800° C. Some physical and mechanical properties of boron-doped HT carbons have been measured and compared with those for boron-free materials. It was confirmed that the boron enters the HT carbon at a relatively low temperature of 1400° C and enhances the densification process of compacts during heat-treatment above 1800° C. The addition of boron caused increases in Young's modulus and thermal conductivity, and decreases in hardness and electrical conductivity of HT carbons. The effects are discussed, and compared with those for graphitizable carbons.
Similar content being viewed by others
References
C. E. Lowell,J. Amer. Ceram. Soc. 50 (1967) 142.
J. M. Davidson,Nucl. Sci. Eng. 26 (1969) 90.
H. M. Murty, D. L. Biederman andE. A. Heintz,Fuel 56 (1977) 305.
A. Oya, R. Yamashita andS. Otani,ibid. 58 (1979) 495.
D. E. Soule, Proceedings of the 5th Conference on Carbon, Vol. 1 (Pergamon Press, New York, 1963) p. 13.
P. Delhaes andMarchand,Carbon 3 (1965) 125.
S. Morozowski,ibid. 4 (1966) 227.
J. Bulawa, S. Morozowski andA. S. Vagh,ibid. 10 (1972) 207.
P. Albert andJ. Parisot, Proceedings of the 3rd Conference on Carbon (Pergamon Press, New York, 1957) p. 467.
R. B. Trask,Fuel 47 (1968) 397.
P. Wagner andJ. M. Dikinson,Carbon 8 (1970) 313.
M. Eslik andD. J. Bacon, Proceedings of the 5th Industrial Carbon and Graphite Conference 1977 (Society of Chemical Industry, London, 1978) p. 63.
V. N. Rakyeyeva, A. V. Dyemin, I. F. Nikolbskaia andG. A. Sfipkov,Tsvyetn Myetally 43 (1969) 73.
I. Ogawa, H. Yosida andK. Kobayashi,J. Mater. Sci. 16 (1981) 3181.
I. Ogawa, T. Hagio, H. Yoshida andK. Kobayashi,Yogyo-kyokai-shi 92 (1984) 392 (in Japanese).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Hagio, T., Ogawa, I. & Kobayashi, K. Effects of boron addition on some properties of hard-type carbons. J Mater Sci 21, 4147–4150 (1986). https://doi.org/10.1007/BF01106521
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01106521