Abstract
An electrochemical method based on analyzing the potential-current curves, plotted at various applied PO 2 for an alumina scale developed at 1100°C on a β-NiAl alloy, was used to determine transport parameters in the scale. The variation of Vo vs PO 2 indicates that the scale consists of an inside zone characterized by an ionic-transport number ti∼0.4 and an outside part with ti∼0.1. This leads to a value of the oxygen pressure at the NiAl/Al2O3 interface ∼2×10−27 atm, not far from the equilibrium value. The variation of the oxygen chemical potential inside the scale was determined, showing a steep variation of µO in the middle of the scale. The calculated oxidation constant is close to the experimental one, which would indicate that mainly charged species are responsible for the alumina scale growth.
Similar content being viewed by others
References
J. S. Sheasby and D. B. Jory,Oxid. Met. 12, 527 (1978).
J. S. Sheasby and J. G. Grandsen, Proc. 6th Cong. Met. Corr., Sydney, Australia, 1975, p. 4.
R. R. Dils and P. S. Follansbee, Pratt and Whitney Aircraft Report, 74-005, 1974.
G. Ben Abderrazik, F. Millot, G. Moulin, and A. M. Huntz,J. Am. Ceram. Soc. 68, 307 (1985).
D. Nicolas-Chaubet, A. M. Huntz, and F. Millot,J. Mater. Sci. 26, 6113 (1991).
D. Nicolas-Chaubet, A. M. Huntz, and F. Millot,J. Mater. Sci. 26, 6119 (1991).
J. Balmain and A. M. Huntz,Oxid Met. to be published.
G. Ben Abderrazik, F. Millot, G. Moulin, and A. M. Huntz,J. Am. Ceram. Soc. 68, 302 (1985).
D. Nicolas-Chaubet, thesis, University of Paris XI, Orsay, 1989.
A. Steiner and K. L. Komarek,Trans. Met. Soc. AIME 230, 786 (1964).
El Aïat and F. A. Kröger,J. Am. Ceram. Soc. 65, 280 (1982).
D. Prot and C. Monty,Phil. Mag. A, part II, to be published in 1996.
M. K. Loudjani, A. M. Huntz, and R. Cortès,J. Mater. Sci. 28, 6466 (1993).
J. S. Chen and F. A. Kröger,J. Mater. Sci. 20, 3191 (1985).
C. R. Koripella and F. A. Kröger,J. Phys. Chem. Soc. 47, 55 (1986).
M. Le Gall, A. M. Huntz, B. Lesage, C. Monty, and J. Bernardini,J. Mater. Sci. 29, (1994).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Balmain, J., Huntz, A.M. Improvement of the application of an electrochemical method for the determination of transport properties of an alumina scale. Part I: Alumina scale on aβ-NiAl alloy. Oxid Met 45, 183–196 (1996). https://doi.org/10.1007/BF01046825
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF01046825