Abstract
Liquid and solid alloys in the Au−Cd system were investigated between 60 and 90 at % Cd and 653°–873°K by theemf method, and thermodynamic properties were calculated. The activities of Cd exhibit strong negative deviations from ideal behavior. Partial molar enthalpies are negative and become less so with increasing temperature; partial molar entropies are positive and increase with increasing temperature. A consistent set of integral thermodynamic data for liquid solutions of the entire Au−Cd system at 1000°K were calculated using values taken from the literature. Activities for some solid Cd-rich phases were also obtained. From discontinuities in theemf vs. temperature curve temperatures of phase transitions were determined.
Zusammenfassung
Flüssige und feste Legierungen im System Au−Cd wurden von 60 bis 90 At% Cd zwischen 653° und 873°K mit derEMK-Methode untersucht und thermodynamische Eigenschaften berechnet. Die Aktivitäten von Cd zeigen stark negative Abweichungen vom idealen Verhalten. Die partiellen molaren Enthalpien sind negativ und verschieben sich mit zunehmender Temperatur zu weniger negativen Werten, die partiellen molaren Entropien sind positiv und nehmen mit zunehmender Temperatur zu. Aus eigenen Werten und Literaturdaten wurden integrale thermodynamische Größen für die Schmelzen im gesamten System Au−Cd bei 1000°K berechnet. Für einige feste Cd-reiche Phasen wurden ebenfalls Aktivitäten erhalten und aus den Knickpunkten derEMK-Temperatur-Kurve Temperaturen von Phasenübergängen bestimmt.
Similar content being viewed by others
Author information
Authors and Affiliations
Additional information
Herrn Prof. Dr.H. Nowotny gewidmet.
Mit 5 Abbildungen
Rights and permissions
About this article
Cite this article
Komarek, K.L., Stummerer, G. Thermodynamische Untersuchungen im System Gold—Cadmium. Monatshefte für Chemie 102, 1360–1373 (1971). https://doi.org/10.1007/BF00917192
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF00917192