Hochtemperatur-röntgenographische Untersuchungen an manganreichen Mangan—Vanadin-und Mangan—Chrom—Legierungen

Abstract

The manganese rich portions of the phase diagrams Mn−V and Mn−Cr have been investigated by means of a high temperature X-ray technique. In the system Mn−V two new phases, α′ and β′, have been observed with α-manganese and β-manganese type structure, resp. These phases are probably to be classified as χ-and π-phase. The γ-manganese solid solution with vanadium has a wider range of homogeneity as compared with previous work. The existence of a σ-phase Mn₃V and phase equilibria below 700°C reported previously could be confirmed. The linear thermal expansion of the intermetallic compounds σ, α′, β′, the α-and δ-manganese solid solutions with vanadium has been evaluated. A tentative phase diagram for the manganese rich portion is given. The main features of the system Mn−Cr according to previous investigations could be confirmed. The linear thermal expansion of the σ-phase Mn₃Cr is reported.

Zusammenfassung

Die manganreiche Seite der Systeme Mn−V und Mn−Cr wurde hochtemperatur-röntgenographisch untersucht. Im System Mn−V treten bei 90 At% Mn zwei bisher nicht beobachtete Phasen, α′ und β′, mit α-bzw. β-Manganstruktur auf. Diese gehören möglicherweise der Klasse der χ-bzw. π-Phasen an. Die γ-Mischphase besitzt einen größeren Existenzbereich als in der Literatur angegeben. Die Existenz der σ-Phase Mn₃V, sowie die Phasenzustände bis 80 At% Mn und bei manganreicheren Legierungen unterhalb 700°C werden bestätigt. Das lineare thermische Ausdehnungsverhalten der Phasen σ, α′ und β′ sowie des α-und δ-Mischkristalls werden angegeben. Für den manganreichen Teil wird ein vorläufiges Zustandsdiagramm entworfen. Im System Mn−Cr konnte in großen Zügen Über-einstimmung mit Literaturangaben gefunden werden. Es wird das lineare thermische Ausdehnungsverhalten der σ-Phase Mn₃Cr angegeben.