Neue K-Boride und verwandte Phasen (Re₃B-Typ, aufgefüllt)

Abstract

The crystal structure of the K(Kappa)-Hf−Mo−B-phase has been refined by means ofWeissenberg-photographs; the position 2 a) (P6₃/mmc) is occupied by Mo-atoms (not boron atoms). Thus structural identity with Co₂Al₅ and Mn₃Al₁₀ resp. is obvious. The isotypic K-borides Zr₉Mo₄B (it forms complete solid solutions with Hf₉Mo₄B) and Zr₉W₄B also exist. Hf₉Mo₄B dissolves aluminum up to 14 at% (1400°C).

Further compounds with the abovementioned structure type (K-phases) have been detected within the systems Zr−Mo−{Fe, Co, Ni} and Hf−Mo(W)−{Fe, Co, Ni}; the iron metal atoms occupy the boron positions.

Phases with composition Zr₃{Fe, Co, Ni} (N, O) _x , obtained by sintering, belong to the filled up Re₃B-type structure.

Zusammenfassung

Mit Hilfe vonWeissenberg-Aufnahmen wird die Kristall-struktur der K(Kappa)-Hf−Mo−B-Phase verfeinert. Die Punktlage 2 a) in P6₃/mmc ist durch Mo-Atome (nicht Boratome) aufgefüllt. Damit entsteht praktisch Strukturgleichheit mit Co₂Al₅ bzw. Mn₃Al₁₀. Die analogen K-Boride Zr₉Mo₄B (mit Hf₉Mo₄B lückenlos mischbar) und Zr₉W₄B bestehen ebenfalls. In Hf₉Mo₄B werden bis 14 At% Al (1400°C) aufgenommen.

In den Systemen Zr−Mo−{Fe, Co, Ni} und Hf−Mo(W)−{Fe, Co, Ni} werden weitere Vertreter mit obigem Strukturtyp (K-Phasen) aufgefunden; die Eisenmetall-Atome treten an Stelle von Bor.

Phasen vom Typ Zr₃{Fe, Co, Ni} (N, O) _x entstehen beim Sintern in mäßigem Vakuum und gehören zur aufgefüllten Re₃B-Struktur.