Röntgenographische Untersuchungen im Dreistoff V−P−C

Abstract

The phase equilibria in the ternary system V−P−C are investigated at 1000°C. A new vanadium phosphide, V₄P₃, has been identified (Nb₄As₃-type, space group Cmem,a =3.261,b=13.23,c=17.30 Å). Five ternary phases have been found: Besides V₃PC_1-x (filled up Re₃B-type) and V₂PC (H-phase) already described, there are the phases V_5+x P₃C_1-x (filled up D8₈-type), orthorhombic V_{≈ 6}P₃C_1-x , and V₄P₂C. The crystal structure of V₄P₂C has been determined (space group P-62m,a =9.567,c =3.166 Å).. V₄P₂C represents a new structure type, which can be described as a dense packing of trigonal prismatic and octahedral building elements.

Zusammenfassung

Es wird die Aufteilung der Phasenfelder bei 1000°C im Dreistoff V−P−C ermittelt. Ein neues Vanadinphosphid V₄P₃ mit Nb₄As₃-Typ (Raumgruppe Cmem,a =3,261,b=13,23,c=17,30 Å) wird sichergestellt. Im Dreistoff existieren neben den bereits beschriebenen Kristallarten V₃PC_1-x (aufgefüllter Re₃B-Typ) und V₂PC (H-Phase) noch die Phasen V_5+x P₃C_1-x (aufgefüllter D8₈-Typ), das orthorhombische V_{≈ 6}P₃C_1-x und V₄P₂C. Die Kristallstruktur von V₄P₂C wird ermittelt (Raumgruppe P-62m,a=9,567,c=3,166 Å). V₄P₂C repräsentiert einen neuen Strukturtyp, der als dichte Packung trigonal prismatischer und oktaedrischer Bauelemente aufgefaßt werden kann.