Abstract
The partial molar free enthalpy of cobalt,\(\Delta \bar G_{Co}\), and the molar free enthalpy of formation of Co x Se alloy phase, ΔG 0f (Co x Se) at 873K, were determined by the solid CaF2 electrolyte galvanic cell method forx=0.725 to 0.956.\(\Delta \bar G_{Co}\) was observed to be a monotonic function of the mole fractionX Co in the composition region of the investigation with an inflexion point atX Co=0.455. The measurements were extended down to a temperature of 710 K and a partial Co−Se phase diagram was evaluated from the resultant data.
Zusammenfassung
Die partiellen molaren freien Enthalpien von Kobalt (\(\Delta \bar G_{Co}\)) und die molaren freien Bildungsenthalpien der Co x Se Legierungsphase [ΔG f/0 (Co x Se) bei 873 K] wurden mittels galvanischer Zelle (CaF2 Fest-Elektrolyt) fürx=0,725–0,956 bestimmt.\(\Delta \bar G_{Co}\) wurde im untersuchten Bereich als monotone Funktion vom MolenbruchX Co, mit einer Inflexion beiX=0,455, gefunden. Die Messungen wurden bis zu einer Temperatur von 710 K ausgedehnt und die Daten wurden zur Erstellung eines partiellen Co−Se-Phasendiagramms ausgewertet.
Similar content being viewed by others
References
N. G. Eror andJ. B. Wagner, jr., Acta Met.11, 1339 (1963).
K. Igaki andY. Noda, Nippon Kinzoku Gakkaishi33, 371 (1969).
Y. Noda andK. Igaki, Ibid.35, 1031 (1971).
M. Laffitte andO. Cerclier, High Temp. and High Pressure1, 449 (1969).
O. B. Matlasevich andV. A. Geiderikh, J. Fiz. Khim.46, 1829 (1972).
O. B. Matlasevich, V. A. Geiderikh, andYa. I. Gerassimov, Rev. Chim. Mineral9, 191 (1972).
H. Jelinek andK. L. Komarek, Mh. Chem.105, 689 (1974).
F. Bohm, F. Gronvold, H. Haraldsen, andH. Pydz, Acta Chem. Scand.9, 1510 (1955).
K. L. Komarek andK. Wessely, Mh. Chem.103, 896 (1972).
R. Gee andR. A. J. Shelton, Trans. Inst. Min. Met.80, C-192 (1971).
G. Chattopadhyay, M. D. Karkhanavala, andM. S. Chandrasekharaiah, J. Electrochem. Soc.122, 325 (1975).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Chattopadhyay, G., Chandrasekharaiah, M.S. & Karkhanavala, M.D. Thermodynamic stability of the γ-Co1−x Se phase by CaF2 electrolyte galvanic cell method. Monatshefte für Chemie 109, 1349–1363 (1978). https://doi.org/10.1007/BF00906048
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF00906048