Abstract
The results presented are of an investigation into the electrical properties of sublimated zinc telluride films of the cubic modification obtained under various conditions of production. The electrical resistivity and the thermo-emf were measured on test specimens at room temperature, and the sign of the current carriers was determined. The dependence of the resistivity on the specimen thickness, on the temperature of preliminary heating of the substrate on which the film was deposited, and on the evaporation temperature was studied. In addition the temperature dependence of the electrical conductivity of layers obtained under various conditions of deposition was investigated. It was established that the thermo-emf coefficient and the specific conductivity of zinc telluride films depend to a considerable extent on the conditions under which they were prepared. The differences that were found were attributed to a change in the stoichiometric composition of the test specimens.
Similar content being viewed by others
References
M. V. Kot and A. V. Simashkevich. Uch. zap. Kishinevskogo un-ta,55, 11–13, 1960.
B. I. Boltaks, O. A. Matveev, and V. P. Savinov, ZhTF,25, 12, 2097, 1955.
J. Horak, M. Machovec, and F. Kosek, Ces. casop. fus.,7, no., 4, 361, 1957.
P. P. Konorov and I. B. Shevchenko, FTT,2, 6, 1960.
B. T. Kolomiets and A. A. Mal'kova, ZhTF,28, no. 8, 1958.
Handbook of Electrotechnical Materials [in Russian],2, 219, 378, Gosenergoizdat, Moscow and Leningrad, 1960.
A. A. Kudryavtsev, Chemistry and Technology of Selenium and Tellurium [in Russian], 71, Vysshaya shkola, Moscow, 1961.
G. A. Zholkevich, Uch. zap. Vologodskogo gospedinstituta,23, 1958.
M. V. Kot and V. G. Tyrziu, Uch. zap. Kishinevskogo universiteta,55, 14–18, 1960.
R. H. Bube, Proc. IRE,43, 12, 1836, 1955.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Shalimova, K.V., Spynulesku, I. & Pirogova, N.V. The effect of the conditions of preparing thin zinc telluride films on their electrical properties. Soviet Physics Journal 9, 83–86 (1966). https://doi.org/10.1007/BF00818502
Issue Date:
DOI: https://doi.org/10.1007/BF00818502