Summary
The electrochemical behaviour of pure indium in KOH solutions (1–4M) was studied at different temperatures (25–70°C) by potentiostatic techniques. Two anodic peaks corresponding to the formation of In(OH)3 and In2O3 were observed. The heights of the two peaks increased with the increase of alkali concentration. An increase of temperature increased the peak currents and shifted their corresponding potentials to more negative values. The variation of the peak currents and peak potentials with scan rate suggested that the anodic dissolution of indium was a diffusion controlled process. In cyclic voltammetry, the reverse scan consistently showed one peak which was attributed to the reduction of anodic oxidation products into indium. X-ray diffraction analysis confirmed the presence of In(OH)3 at the first anodic peak, In(OH)3 and In2O3 at the second anodic peak and In2O3 in the permanent passive region.
Zusammenfassung
Es wurde das Verhalten von reinem Indium in 1 – 4M KOH-Lösungen bei Temperaturen zwischen 25 und 70°C mittels potentiostatischer Methoden untersucht. Zwei anodische Peaks, entsprechend der Bildung von In(OH)3 und In2O3, traten auf. Die Höhe der beiden Peaks wurde mit zunehmender Alkalikonzentration gesteigert. Eine Temperaturerhöhung verstärkte die Peakströme und verschob die entsprechenden Potentiale zu negativeren Werten. Die Abhängigkeit der Peakströme und Peakpotentiale von der Scangeschwindigkeit legte den Schluß nahe, daß die anodische Lösung von Indium in einem diffusionskontrollierten Prozeß stattfindet. Bei der cyclischen Voltammetrie zeigte der reverse Scan einheitlich einen Peak, der der Reduktion der anodischen Oxidationsprodukte zu Indium zugeschrieben wurde. Röntgendiffraktionsanalyse bestätigte die Präsenz von In(OH)3 beim ersten anodischen Peak, In(OH)3 beim zweiten Peak und In2O3 im permanent passiven Bereich.
Similar content being viewed by others
References
Pointelli R., Poli G. (1950) Compt. Rend. Reunion: 136
McElroy A. D., Kleinberg J., Davison A. W. (1952) J. Am. Chem. Soc.74: 736
Glicksman R., Morehouse C. K. (1957) J. Electrochem. Soc.104: 589
Popova T. I., Simonova N. A. (1963) Izvest. Akad. Nauk. S.S.S.R. Ser. Khim: 1187
Amirkhanova N. A., Fizullin F. F. (1964) Electrolitov. Kazan Sbornik: 98
Visco R. E. (1965) J. Electrochem. Soc.112: 932
Fizullin F. F., Amirkhanova N. A. (1965) Sbornick Aspirant-skikh Rabot, Kazansk Gas. Univ: 162
Murtazaer A. M., Nikol Skaya K. Ya. (1964) Dokl. Akad. Nauk. Uzbek S.S.S.R.21: 31
Filippova L. I., Kuzmin L. L. (1969) Izv. Vyssh. Ucheb. Zaved. Khim. Technol.12: 1199
Lewis R. W., Partridge H. H. (1960) Proc. Second Int. Symp. on Batteries, Cournemouth, p. 2
Salem T. M., Ismail A. A. (1970) J. Chem. Soc. (A): 2415
Boswell T. L. (1958) J. Electrochem. Soc.105: 289
Abd El Rehim S. S., Abd El Haleem S. M., Abd El Wahab S. M., Shalaby M. Sh. (1983) Surf. Technol.19: 261
Shams El-Din A. M., Abd El Wahab F. M. (1964) Electrochim. Acta9: 883
Latimer W. M. (1953) Oxidation Potentials, Prentice-Hall, New York
Budov G. M., Losev V. V. (1959) Dokl. Akad. Nauk. S.S.S.R.129: 6
Armstrong R. D., Suttie A. B., Thirsk H. R. (1968) Electrochim. Acta13: 1
Pourbaix M. (1966) Atlas of Electrochemical Equilibria in Aqueous Solutions. Pergamon Press, Oxford, p. 436
El-Tantawy Y. A., Al-Kharafi F. M. (1982) Electrochim. Acta27: 691
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
El Sayed, A., Abd El Rehim, S.S. & Mansour, H. Electrochemical behaviour of an indium electrode in concentrated KOH solutions at different temperatures. Monatsh Chem 122, 1019–1027 (1991). https://doi.org/10.1007/BF00811110
Received:
Revised:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00811110