Monatshefte für Chemie / Chemical Monthly

, Volume 116, Issue 11, pp 1237–1245 | Cite as

The crystal structure of the molybdenum cementite Mo12Fe22C10 (ξ-phase)

  • M. Rapposch
  • E. Kostiner
  • S. F. Wayne
  • H. Nowotny
Anorganische Und Physikalische Chemie

Abstract

The crystal structure of molybdenum cementite Mo12Fe22C10 (ξ-phase) has been determined by means of a single crystal x-ray diffraction study of crystal fragments. The lattice parameters were found to be:a=10.865 (3),b=7.767 (2),c=6.559 (2) Å and β=120.13 (2)°, space group C2/m;Z=1. From the analysis ofPatterson maps and differenceFourier analysis the atomic parameters were derived, yielding a residual ofR=0.059. The crystal structure contains octahedral and triangular prismatic groups which accommodate the carbon atoms in their voids, as is usually found in interstitial compounds. The octahedral building group consists of four Mo- and two Fe-atoms, the triangular prism is built up by four Fe-and two Mo-atoms. The mode of filling of the metal polyhedra is discussed.

Keywords

Crystal structure Complex carbides Mo-cementite 

Die Kristallstruktur von Molybdän-Zementit, Mo12Fe22C10 (ξ-Phase)

Zusammenfassung

Die Kristallstruktur von Molybdän-Zementit, “Mo12Fe22C10” (ξ-Phase) wird auf Grund von Einkristall-Beugungsaufnahmen unter Anwendung vonPatterson-and DifferentialFourier-Analysen bestimmt. In der monoklinen Elementarzelle (a=1.870;b=7.67;c=6.563 Å, β=120.1°) Raumgruppe C 2/m befindet sich eine Formeleinheit Mo12Fe22C10 (oderZ=2, Mo6Fe11C5). DerR-Wert von 6% für 1200 Reflexe unterstreicht die Richtigkeit der Struktur, die aus oktaedrischen und trigonal prismatischen Gruppen aufgebaut ist. Die Oktaedergruppe besteht aus 4 Mo- und 2-Fe-Atomen, die trigonal prismatische Gruppe aus 4 Fe- und 2 Mo-Atomen. Die Kohlenstoffatome füllen die Lücken dieser Bauelemente, wie es für typische Einlagerungscarbide (Komplexcarbide) erwartet werden kann.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    Kuo K., J. Iron Steel Inst.173, 363 (1953);184, 258 (1956).Google Scholar
  2. 2.
    Habraken L., Rev. Met.5, 51 (1954).Google Scholar
  3. 3.
    Dyson D. J., Andrews K. W., J. Iron Steel Inst.191, 325 (1964).Google Scholar
  4. 4.
    Craig B. D., Scripta Met.15, 91 (1981).Google Scholar
  5. 5.
    Wayne S. F., Nowotny H., Rev. Chim. Min.20, 528 (1983).Google Scholar
  6. 6.
    Busing W. R.,Martin K. O.,Levy H. H., ORNL-TM-305 (1962).Google Scholar
  7. 7.
    International Table for X-ray Crystallography, Vol. IV, p. 99. Birmingham: Kynoch Press. 1974.Google Scholar
  8. 8.
    Zachariasen W. H., Acta Crystallogr. Sect.A 23, 558 (1968).Google Scholar
  9. 9.
    See:Pearson W. B., A Handbook of Lattice Parameters and Structures of Metals and Alloys. Oxford: Pergamon Press. 1967.Google Scholar
  10. 10.
    Nowotny H., Angew. Chem.84, 973 (1972).Google Scholar

Copyright information

© Springer-Verlag 1985

Authors and Affiliations

  • M. Rapposch
    • 1
  • E. Kostiner
    • 1
  • S. F. Wayne
    • 1
  • H. Nowotny
    • 1
  1. 1.Institute of Materials Science and Departments of Chemistry and MetallurgyUniversity of ConnecticutStorrsUSA

Personalised recommendations