Thermodynamic properties of liquid bismuth—Lead alloys

Abstract

On liquid Bi—Pb alloys emf measurements were carried out. From the emf data the thermodynamic properties were calculated. In the temperature range between 643 to 923 K no anomalies in the thermodynamic properties were found. The emf varies linearly with temperature and the activity of Pb shows a slight negative deviation fromRaoult's law. However, when ΔH ^M/x is plotted against (1−x) the results are two staight lines which intersect at approximately 35 at% Bi. This could be interpreted that Bi—Pb melts change from one regular behaviour to another.

Zusammenfassung

An flüssigen Wismut—Blei Legierungen wurden EMK-Messungen durchgeführt. Aus den EMK-Daten wurden die thermodynamischen Größen berechnet. Im Temperaturbereich zwischen 643 und 923 K konnte kein anomales Verhalten der thermodynamischen Eigenschaften festgestellt werden. Die EMK steight linear mit der Temperatur und die Aktivität von Pb zeigt eine geringe negative Abweichung vomRaoult'schen Gesetz. Wird jedoch ΔH ^M/x gegen (1—x) aufgetragen, werden zwei Gerade erhalten, die bei ca. 35 At% Bi einen Schnittpunkt aufweisen. Das kann dahin gedeudet werden, daß die Bi—Pb-Schmelze von einer regulären lösung in eine andere übergeht.