Lattice parameters, magnetic properties, and melting behavior of the ternary NiAs-phase in the Ni-Sb-Te system

  • Herbert Ipser
  • Peter Terzieff
Anorganische Und Physikalische Chemie

Abstract

Lattice parameter, magnetic, and DTA-measurements were performed in the range of the ternary NiAs-phase in the nickel-antimony-tellurium system which exhibits a continuous range of homogeneity. Lattice parameter and susceptibility values are reported for three sections with constant ratios ofxSb/xTe=4.00, 1.00, and 0.25. The ternary liquidus projection is given between about 35 and 60 at % Ni.

Keywords

Nickel-antimony-tellurium Phase diagram: Ni-Sb-Te Lattice parameters: Ni-Sb-Te Magnetic properties: Ni-Sb-Te NiAs-Phase: Ni-Sb-Te 

Gitterparameter, magnetische Eigenschaften und Schmelzverhalten der ternären NiAs-Phase im System Ni-Sb-Te

Zusammenfassung

Im Bereich der ternären NiAs-Phase im System Nickel-Antimon-Tellur, welche einen durchgehenden Homogenitätsbereich aufweist, wurden Gitterparameter bestimmt und magnetische Messungen und Differenz-Thermo-Analysen durchgeführt. Werte für die Gitterparameter und für die Suszeptibilität werden auf drei Schnitten mit konstanten VerhältnissenxSb/xTe angegeben, nämlich fürxSb/xTe=4.00, 1.00 und 0.25. Weiters wird die Projektion der ternären Liquidusoberfläche zwischen etwa 35 und 60 At% Ni gezeigt.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. [1]
    Hansen M, Anderko K (1958) Constitution of binary alloys. McGraw-Hill, New York, p 1037Google Scholar
  2. [2]
    Klepp KO, Komarek KL (1972) Monatsh Chem 103: 934Google Scholar
  3. [3]
    Makarov ES (1943) Izv Sekt Fiz-Khim Anal Akad Nauk SSSR 16: 149Google Scholar
  4. [4]
    Gal'perina TN, Zelenin LP, Bashkatov AN, Gel'd PV, Oblasov AK (1976) Izv Akad Nauk SSSR, Neorg Mater 12: 392; Inorg Mater 12: 339Google Scholar
  5. [5]
    Chen T, Rogowski D, White RM (1978) J Appl Phys 49: 1425Google Scholar
  6. [6]
    Leubolt R,Ipser H,Komarek KL, (1986) Z Metallk, in printGoogle Scholar
  7. [7]
    Leubolt R, Ipser H, Terzieff P, Komarek KL (1986) Z anorg allg Chem 533: 205Google Scholar
  8. [8]
    Terzieff P, Schicketanz H, Komarek KL (1986) J Less-Common Met 115: 35Google Scholar
  9. [9]
    Makovetskii GI, Shakhlevich GM (1982) Izv Akad Nauk SSSR, Neorg Mater 18: 226; Inorg Mater 18: 186Google Scholar
  10. [10]
    Barstad J, Grønvold F, Røst E, Vestersjø E (1966) Acta Chem Scand 20: 2865Google Scholar
  11. [11]
    Ettenberg M, Komarek KL, Miller E (1970) J Solid State Chem 1: 583Google Scholar

Copyright information

© Springer-Verlag 1986

Authors and Affiliations

  • Herbert Ipser
    • 1
  • Peter Terzieff
    • 1
  1. 1.Institute of Inorganic ChemistryUniversity of ViennaWienAustria

Personalised recommendations