The cold resistance of weld joints of several construction steels after impulse loading

  • G. N. Nadezhdin
  • S. N. Smirnova
  • Yu. I. Fadeenko
Scientific-Technical Section
  • 25 Downloads

Abstract

Experimental studies have been carried out on the effects of explosion treatment on a number of strength characteristics and the brittle-ductile transition point found in weld joints made of two tube steels. The choosen regime of explosion treatment did not significantly change the values of these characteristics. However, by changing the investigated strength and deformation characteristics, it has been shown possible to estimate the effectiveness of weld joint explosion treatment on tube steels.

Keywords

Experimental Study Transition Point Tube Steel Strength Characteristic Weld Joint 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

Literature cited

  1. 1.
    The Practical Application of Fracture Mechanics to Pressure Vessel Technology, Inst. Mech. Engs., London (1971).Google Scholar
  2. 2.
    S. V. Mak Klaren and K. R. Formen, “The properties of aviation and cosmic materials at low temperatures under conditions of biaxial loading,” in: The Mechanical Properties of Construction Materials at Low Temperatures [in Russian], Metallurgiya, Moscow (1983), pp. 59–70.Google Scholar
  3. 3.
    B. G. Petushkov, Yu. I. Fadeenko, and V. M. Kudinov, “The removal of residual stresses form weld joints using explosion treatment,” in: Transactions of the III Conference on the Explosion Treatment of Materials [in Russian], G. E. Kuz'min (ed.), B. I., Novosibirsk (1982), pp. 103–105.Google Scholar
  4. 4.
    O. A. Shatskaya, E. Yu. Rivkin, V. E. Mozharov, et al., “The fracture resistance of large diameter pipes used In the RBM-K reactor,” in: The Crack Resistance of Materials and Structural Components [in Russian], Naukova Dumka, Kiev (1980), pp. 325–330.Google Scholar
  5. 5.
    E. Sugie, M. Matsuoka, T. Akiyata, et al., “The evaluation of shear fracture propagation and the influence of separation in high strength line pipe,” J. Iron Steel Inst. Jpn.,69, No. 9, 1190–1197 (1983).Google Scholar
  6. 6.
    O. M. Ivantsov and V. I. Kharitonov, The Reliability of Large Diameter Pipes [in Russian], Nedra, Moscow (1978).Google Scholar
  7. 7.
    A. Ya. Krasovskii and G. N. Nadezhdin, “The physical meaning of temperature in brittleness,” in Transactions of the III All-Union Conference on The Physics of Brittle Failure [in Russian], The Institute of Material Behavior, Kiev (1976), pp. 27–30.Google Scholar
  8. 8.
    A. Ya. Krasovskii, G. N. Nadezhdin, V. N. Drasiko, et al., “The effect of weld joint explosion treatment on the strength and crack resistance of several structural steels based on an analysis of the structural state of the material,” in: Transactions of the III International Conference on the High Speed Treatment of Materials [in Russian], B. I., Novosibirsk (1986), pp. 79–84.Google Scholar
  9. 9.
    B. G. Pitushkov, Yu. I. Fadeenko, E. Ya. Lokshina, et al., “Changes in the structure and properties of weld joints after explosion treatment,” in: Transactions of the III International Conference on High Speed Treatment of Materials [in Russian], B. I., Novosibirsk (1986), pp. 101–106.Google Scholar

Copyright information

© Plenum Publishing Corporation 1993

Authors and Affiliations

  • G. N. Nadezhdin
    • 1
  • S. N. Smirnova
    • 1
  • Yu. I. Fadeenko
    • 1
  1. 1.Strength of Materials InstituteUkrainian Academy of SciencesUSSR

Personalised recommendations