Conclusions
It was shown in the investigation that SAP foil can be produced by direct rolling of the powder (ASP-1 powder). The processes consist of cold compacting rolling of the powder, sintering, intermediate rolling, and cold rolling.
During the experiments on rolling of powder ASP-1, the dependence of the strip thickness on the fill ratio for SAP was determined. The data obtained are very close to the results published by G. A. Vinogradov for pure aluminum.
Similar content being viewed by others
Literature cited
Collection: Heat-Resistant Material from Sintered Aluminum Powder SAP [in Russian], edited by I. N. Fridlyander and B. I. Matveev, Oborongiz, M. (1961).
V. A. Shelamov, Otraslevoi zhurnal, 2, 43 (1962).
V. A. Shelamov, Byulleten TsHNTsvetmet, 2, 41 (1962).
P. T. Vlasova, B. I. Matveev, et. al., Otraslevoi zhurnal, 8, 18 (1962).
E. B. Lozhechnikov, Promyshlennost's Belorussii, 11, 39 (1962).
E. B. Lozhechnikov, New Techniques and Progressive Technology [in Russian], Izd. Min. vysshego i srednego spets. i prof, obrazovaniya BSSR, Minsk, 53 (1963).
G. A. Vinogradov and Yu. N. Semenov, Rolling of Metal Powders [in Russian], Metallurgizdat, M. (1960).
G. A. Vinogradov, Poroshkovaya Metallurgiya, 4 (1962).
Collection: Aluminum Alloys [in Russian], edited by I. N. Fridlyander, Part II. Sintered Alloys, Oborongiz, M. (1963).
Rights and permissions
About this article
Cite this article
Shelamov, V.A. On the possibility of producing sap foil by powder boiling. Powder Metall Met Ceram 4, 170–172 (1965). https://doi.org/10.1007/BF00777023
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF00777023