The kinetics of body steel KP60 failure are studied in the final stages of deformation with static tension for smooth specimens and with stress concentrators. Attention is concentrated on features of the generation and start of separation macrocracks in test specimens. Common and distinctive features of damage formation in the test steel are noted taking account of the form of stressed state.
Similar content being viewed by others
Literature cited
J. R. Rice and D. M. Tracey, “On the ductile enlargement of voids in triaxial stress fields,” J. Mech. Phys. Sol.,17, No. 3, 201–217 (1969).
Gerson, “Continuum theory of ductile failure caused by formation and growth of pores. Part 1. Flow criteria and flow rules for a porous ductile material,” Teor. Osn. Inzh. Raschetov, No. 1, 1–17 (1977).
P. Gilormini, C. Licht, and P. Suguet, “Growth of voids in a ductile matrix: a review,” Arch. Mech.,40, No. 1, 43–80 (1988).
M. J. Worswick and R. J. Rick, “Void growth and constitutive softening in a periodically voided solid,” J. Mech. Phys. Sol,38, No. 5, 601–625 (1990).
B. I. Koval'chuk, A. A. Lebedev, and S. É. Umanskii, Mechanics of Inelastic Deformation of Materials and Structural Elements [in Russian], Naukova Dumka, Kiev (1987).
A. A. Lebedev, N. G. Chausov, and L. V. Zaitseva, “Effect of the form of stressed state on failure kinetics and cracking of maraging steel. Communication 1. Study of the stagewise process of failure,” Probl. Prochn., No. 8, 3–13 (1991).
A. A. Lebedev, O. I. Marusii, N. G. Chausov, and L. V. Zaitseva, “Study of Failure kinetics for ductile materials in the concluding stage of deformation,” Probl. Prochn., No. 1, 12–18 (1982).
O. I. Marusii, N. G. Chausov, and L. V. Zaitseva, “Effect of crystallographic orientation on the failure of alloy ZhS6F single crystals,” Probl. Prochn., No. 5, 86–90 (1984).
A. A. Lebedev, N. G. Chausov, O. I. Marusii, et al., “Failure kinetics for sheat ductile material in the concluding stage of deformation,” Probl. Prochn., No. 12, 18–25 (1988).
N. G. Chausov, “Instability of macrocrack growth in plane specimens of ductile materials,” Probl. Prochn., No. 6, 15–18 (1988).
N. G. Chausov, Yu. L. Evetskii, and A. A. Lebedev, “Failure kinetics for thin sheet ductile materials with nonisothermal loading,” Probl. Prochn, No. 2, 12–16 (1989).
A. A. Lebedev, N. G. Chausov, O. I. Marussii, et al, “Failure kinetics for sheet austentic steel in the concluding stage of deformation,” Probl. Prochn, No. 3, 16–21 (1989).
A. A. Lebedev and N. G. Chausov, “Device for testing materials with construction of the total uniform deformation diagram,” Probl. Prochn, No. 12, 104–106 (1981).
P. Bridgeman, Study of High Plastic Strains and Breaking [Russian translation], Izd. Inostr. Lit., Moscow (1955).
A. A. Lebedev, N. G. Chausov, and L. V. Zaltseva, “Effect of the form of stressed state on failure kinetics and cracking of maraging steel. Communication 2. Evaluation of steel crack resistance,” Probl. Prochn, No. 8, 14–18 (1991).
Author information
Authors and Affiliations
Additional information
Translated from Problemy Prochnosti, No. 3, pp. 3–9, March, 1993.
Rights and permissions
About this article
Cite this article
Chausov, N.G., Lebedev, A.A., Zaisteva, L.V. et al. Effect of the form of stressed state on the kinetics of damage accumulation and crack resistance of body steel 15Kh2MFA under different conditions. Communication 1. Stagewise process of steel KP60 failure. Strength Mater 25, 157–162 (1993). https://doi.org/10.1007/BF00776858
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF00776858