Abstract
The results are presented of investigations into 09G2S, 10KhSND, St20, VSt.3sp, and St-38-b2 (East Germany) steels and welded joints to determine cyclic cracking resistance at temperatures of +20 and −70°C taking into account the nature of the loading cycle of metal structures in lifting machines.
Access this article
We’re sorry, something doesn't seem to be working properly.
Please try refreshing the page. If that doesn't work, please contact support so we can address the problem.
Similar content being viewed by others
Literature cited
RD 50-345-82. Procedure Instructions. Strength Calculations and Tests. Methods of Mechanical Testing of Metals. Determination of Cracking Resistance (Fracture Toughness) Characteristics in Cyclic Loading [in Russian], Issued 01.01.83.
O. P. Ostash, “Special features of the method of examining the kinetics of low-temperature fatigue failure,” in: Methods and Means of Evaluating the Cracking Resistance of Structural Materials [in Russian], Naukova Dumka, Kiev (1981), pp. 231–234.
O. P. Ostash and V. T. Zhmur-Klimenko, “Fatigue crack growth at low temperatures (review),” Fiz. Khim. Mekh. Mater., No. 2, 17–29 (1987).
O. P. Ostash, V. T. Zhmur-Klimenko, E. M. Kostyk, and A. B. Kunovskii, “Effect of crack closure and stress ratio on the kinetic diagrams of fatigue failure,” Fiz. Khim. Mekh. Mater., No. 3, 58–63.
A. Ya. Krasovskii, Brittleness of Metals at Low Temperatures [in Russian], Naukova Dumka, Kiev (1980).
O. P. Ostash, V. T. Zhmur-Klimenko, S. Ya. Yarema, et al., “Low-temperature cyclic cracking resistance of welded joints in Fe-Cr-Ni and Fe-Cr-Mn steels,” Fiz. Khim. Mekh. Mater., No. 3, 39–43 (1983).
Author information
Authors and Affiliations
Additional information
Translated from Problemy Prochnosti, No. 10, pp. 8–11, October, 1990.
Rights and permissions
About this article
Cite this article
Pustovoi, V.N. Cyclic low-temperature cracking resistance of structural steels and welded joints in metal structures. Strength Mater 22, 1388–1393 (1990). https://doi.org/10.1007/BF00767217
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF00767217