Abstract
We report on the epitaxial growth of BaCuO2 infinite layer (stabilised with CO3 groups) thin films by rf magnetron sputtering on (100) SrTiO3 and (100) LaAlO3. Excellent (001) films with c∼4Å are obtained at 540 °C in a sputtering atmosphere of 1–10 mTorr of Ar+O2 with some addition of CO2. Off axis x-ray analysis reveal perfect in plane ordering and a tetragonal structure with a=b∼3.96 Å. For these deposition conditions the resistivity at room temperature is of the order of several Ωcm and exhibits a strong semiconductor-like behaviour. When the deposition temperature is increased to 660 °C, a supercell along the c axis appears with a period of about 8Å. After an in-situ annealing of these films in 7 Torr of oxygen at 500 °C, ϱ(300K) falls to 800μΩcm. The resistance versus temperature curve reveals then a metallic behaviour and a superconducting transitions with onsets between 10–40K.
Similar content being viewed by others
References
T. Siegrist et al.,Nature 334, 231 (1988).
M.G. Smithet al.,Letters to Nature 351, 549 (1991).
M. Azuma et al.,Nature 356, 775 (1992).
H. Adachi et al.,Physica C 196, 14 (1992).
E. Koller et al.,Physica C 235–240, 707 (1994).
E. Koller et al.,Journal of Alloys and Compounds 195, 303 (1993).
L. Fabrèga et al., to be published.
Adachi et al.,Physica C 244, 282 (1995).
Y. Miyazaki et al.,Physica C 191, 434 (1992).
J.L. Allen et al.,Physica C 241, 158 (1995)
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Koller, E., Fàbrega, L., Triscone, J.M. et al. Epitaxial growth and properties of (CO3) stabilised BaCuO2 superconducting thin films. J Low Temp Phys 105, 1325–1330 (1996). https://doi.org/10.1007/BF00753884
Issue Date:
DOI: https://doi.org/10.1007/BF00753884