Abstract
The activation energy of two Si3N4/MgO materials, fabricated in the Si3N4-Si2N2O-Mg2SiO4 compatibility triangle of the Si-Mg-O-N system, was determined between 1300 and 1400° C under a compressive stress of 275 MPa. The activation energy of the material previously shown to exhibit pure diffusional creep was determined to be 660 kJ mol−1, whereas the material shown to exhibit extensive cavitational creep had an activation energy of 1080 kJ mol−1. These results are compared with results obtained by others for densification and slow crack growth.
Similar content being viewed by others
References
F. F. Lange, B. I. Davis andD. R. Clarke,J. Mater. Sci. 15 (1980) 601.
F. F. Lange, D. R. Clarke andB. I. Davis,ibid. 15 (1980) 611.
F. F. Lange, B. I. Davis andD. R. Clarke,ibid. 15 (1980) 616.
D. R. Clarke andF. F. Lange,J. Amer. Ceram. Soc. 63 (1980) 586.
R. Kossowsky, D. G. Miller andE. S. Diaz,J. Mater. Sci. 10 (1975) 983.
M. S. Seltzer,Bull. Amer. Ceram. Soc. 56 (1977) 418.
S. Ud Din andP. S. Nicholson,J. Mater. Sci. 10 (1975) 1375.
R. M. Arons andJ. K. Tien,ibid. 15 (1980) 2046.
J. M. Birch andB. Whilshire,ibid. 13 (1980) 2627.
F. F. Lange, in “Deformation of Ceramic Materials” edited by R. C. Bradt and R. E. Tressler (Plenum Press, New York, 1975) p. 361.
L. J. Bowen, R. J. Weston, T. G. Carruthers andR. J. Brook,J. Mater. Sci. 13 (1978) 341.
G. R. Terwilliger andF. F. Lange,J. Amer. Ceram. Soc. 57 (1974) 25.
R. Raj andP. E. D. Morgan,ibid. 64 (10) (1981) C143.
A. G. Evans andS. M. Wiederhorn,J. Mater. Sci. 9 (1974) 270.
A. G. Evans, L. R. Russell andD. W. Richerson,Met. Trans. 6 (1975) 707.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Lange, F.F., Davis, B.I. Compressive creep of Si3N4/MgO alloys. J Mater Sci 17, 3637–3640 (1982). https://doi.org/10.1007/BF00752208
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00752208