Abstract
A metastable shift of the solubility limit was produced by splat-quenching in Sn-Bi alloys containing 15, 20 and 25 at. % bismuth. Decomposition of the supersaturated a phase was investigated in the temperature range −40 to O° C. An activation energy of 39.8±3.0 kJ mol−1 was obtained for the decomposition of Sn-25 at. % Bi. Splat-quenched Cu-Sb alloys with different compositions were also studied. The decomposition of the retainedβ high-temperature phase was followed at 200 and 330° C. Neither an increase of solubility of copper into antimony nor new phases at the eutectic composition were observed in quenched foils.
Similar content being viewed by others
References
M. Hansen andK. Anderko, “Constitution of Binary Alloys” (McGraw-Hill, New York, 1958).
R. H. Kane, B. C. Giessen andN. J. Grant,Acta Met. 14 (1966) 605.
R. Elliott, “Constitution of Binary Alloys”. 1st Suppl. (McGraw-Hill, New York, 1965).
W. Hofmann,Z. Metallk. 33 (1941) 373.
B. C. Giessen, U. Wolff andN. J. Grant,Trans. Met. Soc. AIME 242 (1968) 597.
E. Laine, E. Heikkilä andI. Lâhteenmäki,Rev. Sci. Instr. 42 (1971) 1724.
E. Laine, I. Lähteenmäki andM. Kantola,X-Ray Spectrom. 1 (1972) 93.
E. Laine andI. Lähteenmäki,Kemian Teollisuus 30 (1973) 381.
E. Laine, I. Lähteenmäki andM. Hämäläinen,J. Phys. E: Sci Instr. 7 (1974) 951.
B. Predel andG. Schluckebier,Z. Metallk. 63 (1972) 198.
E. Günzel andK. Schubert,ibid 49 (1958) 124.
H. Jones,Rep. Prog. Phys. 36 (1973) 1425.
S. Yamaguchi andM. Hirabayashi,J. Phys. Soc. Japan 33 (1972) 708.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Laine, E., Lähteenmäki, I. & Lehtoranta, I. An X-ray study of splat-quenched Sn-Bi and Cu-Sb alloys by energy-dispersive diffraction. J Mater Sci 13, 108–112 (1978). https://doi.org/10.1007/BF00739280
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00739280