Mechanism of the effect of hydrogen on fatigue crack propagation in structural steels
- 23 Downloads
KeywordsHydrogen Fatigue Fatigue Crack Structural Steel Fatigue Crack Propagation
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.
Unable to display preview. Download preview PDF.
- 1.O. N. Romaniv, G. N. Nikiforchin, and L. Yu. Kozak, “Cyclic cracking resistance of structural steels in gaseous hydrogen,” Fiz.-Khim. Mekh. Mater., No. 5, 3–15 (1986).Google Scholar
- 2.A. Ohta and E. Sasaki, “Plastic zone around fatigue cracks of pure iron in vacuum and dry air,” Acta Metall.,20, No. 5, 657–660 (1972).Google Scholar
- 3.N. M. Grinberg, “Fatigue crack growth in vacuum,” in: Fatigue Crack Propagation Resistance of Metallic Alloys Used in Railroad Transport [in Russian], Transport, Moscow (1984).Google Scholar
- 4.V. I. Pokhmurskii and L. N. Bilyi, “Kinetics of fatigue cracks in iron in electrolytic hydrogen in charging,” Fiz.-Khim. Mekh. Mater., No. 6, 45–48 (1984).Google Scholar
- 5.E. D. Shukin, “Reduction of surface energy and the variation of the mechanical properties of solids under the effect of the environment,” Fiz.-Khim. Mekh. Mater., No. 1, 3–20 (1976).Google Scholar
- 6.M. M. Shved, Variation of the Service Properties of Iron and Steel Under the Effect of Hydrogen [in Russian], Naukova Dumka, Kiev (1985).Google Scholar
- 7.O. N. Romaniv, A. N. Tkach, and V. N. Simin'kovich, “Structure and near-threshold fatigue of steels,” Fiz.-Khim. Mekh. Mater., No. 4, 15–33 (1983).Google Scholar
- 8.P. McIntyre, “Interaction between hydrogen and steel during cyclic loading,” in: Corrosion Fatigue of Metals, Proceedings of a Soviet-British Seminar, Naukova Dumka, Kiev (1982), pp. 121–147.Google Scholar
© Plenum Publishing Corporation 1988