Influence of load cycle asymmetry and overloading on fatigue crack growth rate in stainless steels

  • A. A. Popov
  • E. I. Mamaeva
  • G. A. Drobakhin
  • T. K. Kashirina
Article

Keywords

Growth Rate Fatigue Stainless Steel Fatigue Crack Crack Growth Rate 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

Literature cited

  1. 1.
    P. Romvari, L. Tot, and D. Nad', “An analysis of the rules of fatigue crack propagation in metals,” Probl. Prochn., No. 12, 18–28 (1980).Google Scholar
  2. 2.
    W. Elber, “Fatigue crack closure under cyclic tension,” Eng. Fract. Mech.,2, No. 1, 35–45 (1970).Google Scholar
  3. 3.
    W. Elber, “The significance of fatigue crack closure,” in: Damage Tolerance in Aircraft Structures. ASTM STP 486, ASTM, Philadelphia (1971), pp. 230–242.Google Scholar
  4. 4.
    I. Schijve, “Four lectures on fatigue crack growth,” Eng. Fract. Mech.,11, No. 1, 182–196 (1979).Google Scholar
  5. 5.
    A. A. Popov and E. I. Mamaeva, “An investigation of the kinetics of fatigue crack growth in weld joints of chrome-nickel stainless steel with different loading asymmetries,” in: Summaries of Stand Papers of the 8th All-Union Conference on the Fatigue of Metals [in Russian], Moscow (1982), pp. 88–89.Google Scholar
  6. 6.
    O. N. Romaniv, “Evaluation of the service reliability of metals and alloys,” Metalloved. Term. Obrab. Met., No. 12, 6–13 (1982).Google Scholar
  7. 7.
    K. D. Unangst, T. T. Shih, and R. P. Wei, “Crack closure in 2219-T851 aluminum alloy,” Eng. Fract. Mech.,9, No. 3, 725–734 (1977).Google Scholar
  8. 8.
    A. Ohta, M. Kosuge, and E. Sasaki, “Fatigue crack closure over the range of stress ratios from −1 to 0.8 down to stress intensity threshold level in HT80 steel and SUS 304 stainless steel,” Int. J. Fract.,14, No. 3, 251–264 (1978).Google Scholar
  9. 9.
    R. P. Wi, N. E. Fenelly, K. D. Unangst, and T. T. Shih, “The influence of a large shortterm overload on subsequent fatigue crack growth in 2219-T85 aluminum alloy,” Teor. Osn. Inzh. Rasch.,102, No. 3, 43–57 (1980).Google Scholar
  10. 10.
    A. B. Zlochevskii, L. A. Bondarevich, and A. N. Shuvalov, “The influence of an intense overload on the kinetics of fatigue crack growth,” Fiz.-Khim. Mekh. Mater., No. 6, 43–47 (1979).Google Scholar
  11. 11.
    W. Dahl and G. Roth, “On the influence of overloads on fatigue crack propagation in structural steels,” in: The Strength of Metals and Alloys: Proceedings of the 8th International Conference, Aachen, 1979, Vol. 2, pp. 1249–1254.Google Scholar
  12. 12.
    I. R. Rice, “Mechanics of crack tip deformation and extension by fatigue,” in: Fatigue Crack Propagation. ASTM STP 415, ASTM, Philadelphia (1967), pp. 247–309.Google Scholar
  13. 13.
    A. A. Popov, E. I. Mamaeva, and G. A. Drobakhin, “An investigation of the influence of loading conditions on the closure of a fatigue crack and the rate of its propagation,” in: Low-Cycle Fatigue-Fracture Mechanics, Survivability, and the Material Requirement of a Structure. Summaries of Papers and Reports for the 4th All-Union Symposium, Krasnodar, 1983 [in Russian], Vol. 1, pp. 129–130.Google Scholar
  14. 14.
    O. N. Romaniv, G. N. Nikiforchin, and B. N. Andrusiv, “The effect of crack closure and evaluation of the cyclic crack resistance of constructional alloys,” Fiz.-Khim. Mekh. Mater., No. 3, 47–61 (1983).Google Scholar
  15. 15.
    S. Suresh, “Micromechanisms of fatigue crack growth retardation following overloads,” Eng. Fract. Mech.,18, No. 3, 577–593 (1983).Google Scholar

Copyright information

© Plenum Publishing Corporation 1986

Authors and Affiliations

  • A. A. Popov
    • 1
  • E. I. Mamaeva
    • 1
  • G. A. Drobakhin
    • 1
  • T. K. Kashirina
    • 1
  1. 1.Scientific and Production UnionCentral Scientific-Research Institute for Machine Building TechnologyMoscow

Personalised recommendations