Role of electrochemical solution and hydrogen embrittlement in cracking of high-strength steels in 3% NaCl solution

  • O. N. Chaplya
  • I. I. Vasilenko
Physicochemical Theory of Deformation and Fracture
  • 26 Downloads

Keywords

Hydrogen Hydrogen Embrittlement Electrochemical Solution 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

Literature cited

  1. 1.
    P. C. Hughes, I. R. Lamborn, and B. B. Leibert, JISI, 728–731 (1965).Google Scholar
  2. 2.
    R. B. Mears, Physical Metallurgy of Stress-Corrosion Fracture, New York (1959), p. 238.Google Scholar
  3. 3.
    B. C. Syrett, Corrosion,27, No. 7 (1971).Google Scholar
  4. 4.
    J. E. Truman, R. Perry, and G. N. Chapman, JISI, 745–756 (1964).Google Scholar
  5. 5.
    H. H. Uhlig, Metal Progress,57, 486–487 (1950).Google Scholar
  6. 6.
    H. P. Leckie and A. W. Loginow, Corrosion,24, No. 9 (1968).Google Scholar
  7. 7.
    C. Edeleanu, Stress-Corrosion Cracking and Embrittlement, Wiley, New York (1956), p. 126.Google Scholar
  8. 8.
    U. R. Evans, Stress-Corrosion Cracking and Embrittlement, Wiley, New York (1956), p. 158.Google Scholar
  9. 9.
    I. L. Rozenfel'd, Z. F. Shustova, V. S. Fridman, G. G. Kuznetsov, M. V. Konradi, and V. A. Emel'yanova, Results of Science, Corrosion and Protection of Metals [in Russian], Vol. 1, VINITI, (1971).Google Scholar
  10. 10.
    S. Barnartt, Corrosion,18, 322 (1962).Google Scholar
  11. 11.
    H. H. Uhlig, Physical Metallurgy of Stress-Corrosion Fracture, New York (1959), p. 121.Google Scholar
  12. 12.
    C. Edeleanu, Stress-Corrosion Cracking and Embrittlement, Wiley, New York (1956).Google Scholar
  13. 13.
    T. P. Khor, in: Corrosion of Water-Cooled Reactor Structural Materials [in Russian], Atomizdat (1965).Google Scholar
  14. 14.
    J. A. Smith, M. H. Peterson, and B. F. Brown, Corrosion,26, No. 12 (1970).Google Scholar
  15. 15.
    B. F. Brown, C. T. Fulli, and E. P. Dahlberg, J. Electrochem. Soc.,116, No. 2, (1969).Google Scholar
  16. 16.
    J. H. Shively, R. F. Hehemann, and A. R. Troiano, Corrosion,23, No. 7 (1967).Google Scholar
  17. 17.
    C. F. Barth, E. A. Steigerwald, and A. R.Troiano, Corrosion,25, No. 9 (1969).Google Scholar
  18. 18.
    C. F. Barth and A. R. Troiano, Corrosion,28, No. 7 (1972).Google Scholar
  19. 19.
    H. J. Bhatt and E. H. Phelps, Corrosion,17, No. 3 (1961).Google Scholar
  20. 20.
    P. C. Hughes, JISI,204, 385–387 (1966).Google Scholar
  21. 21.
    G. V. Karpenko and I. I. Vasilenko, Corrosion Cracking of Steels [in Russian], Tekhnika (1971).Google Scholar
  22. 22.
    G. V. Karpenko, I. I. Vasilenko, M. G. Khitarishvili, and V. S. Fedchenko, Dokl. Akad. Nauk SSSR,185, No. 5 (1969).Google Scholar

Copyright information

© Plenum Publishing Corporation 1975

Authors and Affiliations

  • O. N. Chaplya
    • 1
  • I. I. Vasilenko
    • 1
  1. 1.Physicomechanical InstituteAcademy of Sciences of the Ukrainian SSRL'vov

Personalised recommendations