Abstract
It was possible to examine the tensile behaviour in experimental 30Ni-30Cu-40Mn-based alloys which were modified by alloying additions of aluminium, indium and tin. Namely, the experimental alloys were developed on the basis of crack formation in a commercial nickel-based alloy and microstructural features in nickel-based alloys investigated. The addition was done by substituting only the manganese content (40 wt%) to 35 and 40 wt%. The results indicated that both changes of tensile strength and elongation were obtained with castability values above 94%. Comparison of tensile properties in experimental Ni-Cu-Mn-based alloys studied here showed that the addition of aluminium to the alloys was appropriate to obtain results similar to those for commercial alloys, indicating that the refining of dendrite arm spacing was obtained by aluminium addition.
Similar content being viewed by others
References
A. J. LEWIS,J. Biomed. Mater. Sci. 11 (1977) 447.
Idem, J. Dent. Res. 56 (1977) 631.
S. CIVJAN, E. F. HUGET, G. D. GODFREY, H. LICHTENBERGER and W. A. FRANDK, ibid.51 (1972) 1537.
H. F. MORRIS, K. ASGAR, A. P. ROWE and C. E. NASJLETI,J. Prosthet. Dent. 41 (1979) 388.
P. G. BOSWELL and L. STEVENS,Aust. Dent. J. 25 (1980) 125.
K. WAKASA, M. YAMAKI, A. NAKATSUKA and T. NISHIMURA,Shika Rikougaku Zasshi 22 (1981) 217.
B. I. SOSROSOEDIRDJO, K. WAKASA and K. WAKASA,J. Mater. Sci. 24 (1989) 3667.
K. WAKASA and M. YAMAKI,J. Mater. Sci. Mater. in Med. 1 (1990) 171.
H. MURASAWA,Tsurumi Shigaku 9 (1983) 115.
T. HORIBE and Y. INOUE,Dental Engng. 68 (1984) 31.
Y. ITO, K. DOI, H. AOKI, E. KATO, M. KAMIGURI, S. TAKEHANA, Y. OIKE and J. YOKOI,Aichigakuin Daigaku Shishi 22 (1984) 329.
M. KITO, Y. HONDA, N. KAWAMURA, K. IWAI and J. HASEGAWA,Shika Zairyou Kikai 3 (1984) 508.
W. J. O'BRIEN and G. RYGE, “An outline of Dental Materials and their selection” (Saunders, Philadelphia, 1978) p. 239.
J. W. STANFORD, “Dentist's desk reference: Materials, Instruments and Equipment” (American Dental Association, Chicago, 1981), p. 53.
R. W. PHILLIPS, “Skinner's Science of Dental Materials,” 8th Edn (Saunders, Philadelphia, 1982) p. 367.
A. J. LEVIS,Aust. Dent. J. 20 (1975) 221.
G. BARAN and E. C. WOODLAND,J. Dent. Res. 60 (1981) 1761.
K. IDA,Dental Engng. 67 (1983) 18.
A. J. LEWIS,Aust. Dent. J. 22 (1977) 455.
H. J. HARCOURT, M. RIDDIHOUGH and J. OSBORNE,Brit. Dent. J. 129 (1970) 419.
T. KAMEMIZU,Hotetsu-shi 22 (1978) 135.
A. J. LEWIS,Aust. Dent. J. 23 (1978) 192.
K. WAKASA and M. YAMAKI,J. Mater. Sci. Mater. in Med. 1 (1990) 44.
Idem, Shika Zairyou Kikai 2 (1983) 1.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Wakasa, K., Yamaki, M. Tensile behaviour in 30Ni-30Cu-40Mn-based alloys for a dental application. J Mater Sci: Mater Med 2, 71–76 (1991). https://doi.org/10.1007/BF00703461
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00703461