Conclusions
-
1.
Liquid-phase sintering at temperatures somewhat exceeding the solidus point of KhN45MVKBTYu alloy leads to the formation of a liquid phase close in composition to the compound Ni3Al, that is, γ'-phase.
-
2.
Subsequent production heatings lead to solution of this γ'-phase in γ-phase. The main quantity of γ'-phase is formed by the normal method, as the result of intragranular precipitation. γ'-phase of both forms has a similar composition and is uniformly distributed within the grain. In connection with this it may be assumed that the modern method of production of parts of the powder metallurgy nickel high-temperature-strength alloy eliminates the elements of the cast structure unfavorable for the properties.
Similar content being viewed by others
Literature cited
Ya. E. Geguzin, The Physics of Sintering [in Russian], Nauka, Moscow (1984).
I. M. Fedorchenko and R. A. Andrievskii, Fundamentals of Powder Metallurgy [in Russian], Kiev (1961).
A. A. Bondarev, A. B. Bondarev, and T. M. Kunyavskaya, "The question of selection of the conditions of deformation and heat treatment of high-temperature-strength nickel alloys," Metalloved. Term. Obrab. Met., No. 10, 34–38 (1989).
A. V. Logunov and O. I. Samoilov, "A study of the process of liquid-phase sintering in powder metallurgy high-temperature-Strength Alloys," in: Summaries of Papers for the All-Union Symposium on High-Temperature-Strength Alloys [in Russian], Zvenigorod (1989).
U. Betteridzh, Nimonic-Type High-Temperature-Strength Alloys [in Russian], Metallurgiya, Moscow (1961).
A. P. Gulyaev, L. S. Bulavina, and G. S. Chernyak, "The high-temperature plasticity of high-temperature-strength chromium-nickel alloys," Metalloved. Term. Obrab. Met., No. 5, 27–30 (1979).
Additional information
I. P. Bardin Central Scientific-Research Institute for Ferrous Metallurgy. Scientific-Research Institute for Defectology. Translated from Metallovedenie i Termicheskaya Obrabotka Metallov, No. 8, pp. 51–56, August, 1990.
Rights and permissions
About this article
Cite this article
Gulyaev, A.P., Sergienko, L.P., Logunov, A.V. et al. Features of the structure of a high-temperature-strength nickel alloy after liquid-phase sintering. Met Sci Heat Treat 32, 618–623 (1990). https://doi.org/10.1007/BF00700718
Issue Date:
DOI: https://doi.org/10.1007/BF00700718