Conclusions
-
1.
The temperature at which the transition from blistering to flaking occurs depends on the chemical composition of the steel.
-
2.
Flaking may occur at higher temperatures in ductile heat 1 than in less ductile heats.
Similar content being viewed by others
Literature cited
James L. Scott, Met. Progr.,114, No. 2, 40 (1978).
F. N. Flakus, At. Energy Rev.,13, No. 3, 587 (1975).
S. Das and M. Kaminsky, Radiation Effects on Solid Surfaces, Washington, Am. Chem. Soc., No. 158 (1976), p. 112.
I. N. Afrikanov et al., "Helium blistering at high radiation doses," At. Énerg.,46, No. 3, 165 (1979).
J. Gruber and J. Schneider, Ber. Hahr—Meitner Inst. Kernforsch, Berlin, No. 212 (1977).
V. M. Gusev et al., "ILU ion accelerator to 100 keV with separation of ions by weight," Prib. Tekh. Eksp., No. 4, 19 (1969).
V. M. Gusev et al., "Atomization and blistering of some materials bombarded with hydrogen and helium ions," Fiz. Khim. Obrab. Mater., No. 1, 15 (1976).
B. Kelly, Radiation Damage of Solids [Russian translation], Atomizdat, Moscow (1970).
Additional information
A. A. Baikov Institute of Metallurgy. I. V. Kurchatov Institute of Atomic Energy. Translated from Metallovedenie i Termicheskaya Obrabotka Metallov, No. 10, pp. 53–54, October, 1980.
Rights and permissions
About this article
Cite this article
Bannykh, O.A., Kovneristyi, Y.K., Guseva, M.I. et al. Topography of the surface of Cr-Mn austenitic steels after bombardment with helium ions. Met Sci Heat Treat 22, 768–770 (1980). https://doi.org/10.1007/BF00700579
Issue Date:
DOI: https://doi.org/10.1007/BF00700579