Abstract
Bioabsorbable composites, designed for use as rigid tissue scaffolds, were fabricated by reinforcing free radically cured poly(D,L-lactide) fumarate matrices with absorbable poly(glycolic acid) fibers. To investigate the benefits of an improved fiber/matrix interphase, fiber pretreatments were employed including surface-etching by exposure to mild acidic conditions and incorporation of 3-methacryloxypropyltrimethoxysilane as a coupling agent. SEM of composite fracture surfaces showed that fiber pretreatment yielded improved wetting and encapsulation of the fibers by the matrix resin. The composites fabricated with poly(glycolic acid) fibers which were acid-etched and pretreated with the coupling agent showed an average 41% increase in tensile strength; a representative sample displayed an increase from 73.9 MPa to 105.5 MPa, compared to the composite made from untreated fibers.
Similar content being viewed by others
References
Vacenti, J.P.; Morse, M.A.; Saltzman, W.M.; Domb, A.J.,J. of Ped.Surg.,1988, 23, 3–9.
Cornah, J.; Wallace, J.,Brit. J. of Oral and Maxiofacial. Surg.,1988, 26, 250–254.
Assimos, D.G.; Smith, C.; Schaeffer, A.J.; Carone, F.A.; Grayhack, J.T.,Urol. Res. 1984, 12, 291.
Pitt, C.G.; Gu, Z.; P.,I.; Hendren, R.W.,J. Polym. Sci.: Part A: Polym. Chem.,1987, 25, 955–966.
Ibay, A.C.; Whalley, C.E.; Miller, R.A.; Carr, H., Jr.; Battistone, G.C.,Polym. Mat. Sci. Eng. 1985, 53, 505.
Storey, R.F.; Wiggins, J.S.; Mauritz, K.A.; Puckett, A.D.,J. Poly. Chem Ed., submitted for publication.
Storey, R.F.; Hickey, T.P., submitted to theJ. Polymer Sci., Aug.1992.
Storey, R.F.; Warren, S.C.; Allison, C.J.; Wiggins, J.S.; Puckett, A.D.,Polymer submitted for publication.
Lubin, G.,Handbook of Composites, Reinhold Company Inc.,1982, 368–390.
Dee, L.A.; Biggers, B.L.; Fiske, M.E.,Anal. Chem. 1980, 52, 573.
Storey, R.F.; Wiggins, J.S.; Mauritz, K.A., Puckett, A.D.,ACS Div. Polym. Chem., Polym. Preprs.,31(2), 492 (1990).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Storey, R.F., Shoemake, K.A. Poly(glycolic acid) fiber-reinforced bioabsorbable composites with improved interfacial properties. Polymer Bulletin 31, 331–338 (1993). https://doi.org/10.1007/BF00692960
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00692960