Millimetre-sized hollow spheres of lead zirconate titanate by a sol-gel method

  • Xiaoming Yang
  • T. K. Chaki
Papers

Abstract

Hollow spheres of lead zirconate titanate (PZT) [chemical formula Pb(Zr0.52Ti0.48)O3)], with outer diameter of 1–2 mm and a wall thickness of about 100 μm, were fabricated by gellation of a PZT sol inside solid polymer spheres and then burning the polymer out. Monomodally sized polyacrylamide spheres, with diameter 1.40–1.90 mm, were soaked in a PZT sol, prepared by dissolving Pb(NO3)2, zirconiumn-butoxide and titanium isopropoxide inN, N-dimethylformamide. The absorbed sol was then gelled beneath the surface of the polymer sphere by the action of NH3. Upon calcination of the spheres at 850 °C for 4 h in air, hollow spheres of pure PZT perovskite phase (as identified by X-ray diffraction patterns) were obtained. The density of the hollow spheres was 1.13gcm−3, while that of the wall of the spheres was 3.10g cm−3. The scanning electron microscopic examination of the broken spheres showed that the inner surface of the spheres contained rib-like structures, which provided strength to the hollow spheres. The planar coupling factor,kp, of six hollow spheres, placed at a close-packed arrangement in a plane, was 0.22, indicating the possibility of fabrication of low-density transducer arrays.

Keywords

Perovskite Hollow Sphere Isopropoxide Perovskite Phase Lead Zirconate 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    B. JAFFE, W. R. COOK Jr and H. JAFFE, “Piezoelectric Ceramics” (Academic Press, New York, 1971) pp. 135–171.Google Scholar
  2. 2.
    R. MEYER Jr, H. WEITZING, Q. XU, Q. ZHANG, R. E. NEWNHAM and J. K. COCHRAN,J. Am. Ceram. Soc. 77 (1994) 1669.Google Scholar
  3. 3.
    X. YANG and T. K. CHAKI,Mater. Sci. Eng. in press.Google Scholar
  4. 4.
    E. RUCKENSTEIN and L. HONG,Polymer 74 (1995)36 (1995) 2857.Google Scholar
  5. 5.
    X. YANG and T. K. CHAKI, (1996) unpublished.Google Scholar
  6. 6.
    IRE Standards on Piezoelectric Crystals, “Measurement of Piezoelectric Ceramics”, Proceedings of the IRE (Institute of Radio Engineers, New York, 1961) pp. 1161–69.Google Scholar
  7. 7.
    D. A. BERLINCOURT, D. R. CURRAN and H. JAFFE, in “Physical Acoustics”, Vol. 1, Part A, edited by W. P. Mason (Academic Pres, New York, 1964) pp. 169–257.Google Scholar
  8. 8.
    C. D. E. LAKEMAN and D. A. PAYN,J. Am. Ceram. Soc. 75 (1992) 3091.Google Scholar
  9. 9.
    K. HIGUCHI, K. MIYAZAWA, T. SAKUMA and K. SUZUKI,J. Mater. Sci. 29 (1994) 436.Google Scholar

Copyright information

© Chapman & Hall 1996

Authors and Affiliations

  • Xiaoming Yang
    • 1
  • T. K. Chaki
    • 1
  1. 1.Department of Mechanical and Aerospace EngineeringState University of New YorkBuffaloUSA

Personalised recommendations