Molten cast alumomagnesia refractory materials containing up to 28.3% MgO (MgAl2O4) are investigated. It is shown that materials with 10–15% MgO have a complex structure and phase composition. The latter can be interpreted as a solid solution of corundum and spinel or as a combination of MgO · 2.5Al2O3. The behavior of these materials in molten TK16 and K8 glass is investigated.
Similar content being viewed by others
References
V. K. Pavlovskii, E. K. Romanova, and A. D. Semenov, “High-alumina materials of the Al2O3-CaO system,”Steklo Keram., Nos. 9–10, 5–7 (1994).
V. K. Pavlovskii, E. K. Romanova, and A. D. Semenov, “Structure and phase composition of molten cast materials of the A12O3-B2O3 system,”Steklo Keram., Nos. 11–12, 22–24 (1994).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Pavlovskii, V.K., Romanova, E.K. & Semenov, A.D. Molten cast materials of the Al2O3-MgO system. Glass Ceram 52, 11–13 (1995). https://doi.org/10.1007/BF00679143
Issue Date:
DOI: https://doi.org/10.1007/BF00679143