Abstract
Aluminide and chromaluminide diffusion coatings on nickel and a nickel-base superalloy, EI 867, were subjected to different corrosion tests consisting of oxidation under isothermal and thermal cycling conditions, and oxidation in the presence of fused sodium sulfate. It was found that chromium present in the surface layers of aluminide coatings has a beneficial effect on their resistance to oxidation and hot corrosion.
Similar content being viewed by others
References
E. Godlewska and K. Godlewski,Oxid. Met. 22, 117 (1984).
S. Mrowec and K. Przybylski,Bull. Acad. Sci., Chem. 33, 163 (1985).
H. D. Flicker, US Patent 3.753.668.
H. M. Hindam and W. W. Smeltzer,J. Electrochem. Soc. 127, 1630 (1980).
A. E. Paladino and W. D. Kingery,J. Chem. Phys. 37, 957 (1962).
J. A. Goebel, F. S. Pettit, and G. W. Goward,Met. Trans. 4, 261 (1973).
N. S. Bornstein, M. A. Decrescente, and H. A. Roth,Effect of Vanadium and Sodium Compounds on Accelerated Oxidation of Nickel-Base Alloys, Annual Report, Office of Naval Research, Dept. of the Navy, Washington, D.C., Contract N0014-70-C-0234, NR 036-08911-12-70 (471).
R. L. McCarron, N. R. Lindblad, and D. Chatterji,Corr. 32, 476 (1976).
J. M. Quets and W. H. Dresher,J. Mater. 4, 583 (1969).
H. H. Davis, H. C. Graham and G. F. Uhlig,Met. Trans. 3, 3247 (1972).
S. S. Brenner,J. Electrochem. Soc. 102, 16 (1955).
M. M. P. Janssen and G. D. Rieck,Trans. Met. Soc. AIME 239, 1372 (1967).
R. Pichoir,High Temp. Alloys for Gas Turbines, D. Coutsouradis et al., eds. (Applied Science Publishers, London, 1978), pp. 191–209.
J. M. N. Gandu-Muamba, Ph.D. Thesis, Marseille, 1980.
E. Fitzer and H. J. Maurer,Arch. Eisenhuttenwes.49, 95 (1978).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Godlewski, K., Godlewska, E. Effect of chromium on the protective properties of aluminide coatings. Oxid Met 26, 125–138 (1986). https://doi.org/10.1007/BF00664277
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF00664277