Oxidation of Metals

, Volume 21, Issue 5–6, pp 271–284 | Cite as

On the influence of cold work on the oxidation behavior of some austenitic stainless steels: High temperature oxidation

  • J. C. Langevoort
  • T. Fransen
  • P. J. Geilings
Article

Abstract

AISI 304, 314, 321, and Incoloy 800H have been subjected to several pretreatments: polishing, milling, grinding, and cold drawing. In the temperature range 800–1400 K, cold work improves the oxidation resistance of AISI 304 and 321 slightly, but has a relatively small negative effect on the oxidation resistance of AISI 314 and Incoloy 800H. Milling results in an enlargement of the surface area with a factor 2.5.

Key Words

oxidation stainless steel cold work 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    S. J. Allan and M. J. Dean, inBehaviour of High Temperature Alloys in Aggressive Environments I. Kirmann et al., eds., Proc. Int. Conf. Petten (The Metals Society, London, 1979), p. 139.Google Scholar
  2. 2.
    A. Cigada, N. Mazza, P. Pedeferri, G. Salvago, D. Sinigaglia, and G. Zanni,Corr. Sci. 22, 559 (1982).Google Scholar
  3. 3.
    S. Leistikow, in ref. 1 p. 197.Google Scholar
  4. 4.
    R. Stevens,Oxid. Met. 13, 71 (1979).Google Scholar
  5. 5.
    J. C. Langevoort, T. Fransen, and P. J. Gellings,Werkstoffe und Korrosion 34, 500–504 (1983).Google Scholar
  6. 6.
    G. J. Stokkers, A. van Silfhout, G. A. Bootsma, T. Fransen, and P. J. Gellings,Corr. Sci. 23, 195 (1983).Google Scholar
  7. 7.
    S. Pednekar and S. Smialowska,Corrosion 36(10), 56–577 (1980).Google Scholar
  8. 8.
    D. Caplan and M. Cohen,Corr. Sci. 6, 321 (1966).Google Scholar
  9. 9.
    D. Caplan and G. I. Sproule,Oxid. Met. 9, 459 (1975).Google Scholar
  10. 10.
    K. Ledjeff, A. Rahmel, and M. Schorr,Oxid. Met. 15, 485 (1981).Google Scholar
  11. 11.
    R. J. Pearce and R. K. Wild,J. Nucl. Mat. 91, 156–170 (1980).Google Scholar
  12. 12.
    T. Fransen, M. A. de Jongh, and P. J. Gellings, inProc. 8th ICMC Mainz (1981), p. 730.Google Scholar
  13. 13.
    J. Kivel, F. C. Albers, D. A. Olsen, and R. E. Johnson,J. Phys. Chem. 67, 1235 (1963).Google Scholar
  14. 14.
    C. O. Timmons,J. Colloid Interface Sci. 43, 1 (1973).Google Scholar

Copyright information

© Plenum Publishing Corporation 1984

Authors and Affiliations

  • J. C. Langevoort
    • 1
  • T. Fransen
    • 1
  • P. J. Geilings
    • 1
  1. 1.Department of Chemical TechnologyTwente University of TechnologyAE EnschedeThe Netherlands

Personalised recommendations