Abstract
The electrical resistivity and thermoelectric power in annealed and cold-worked samples of Al and Al-Mg alloy have been measured between1.5 and8.5 K. The deviation from Matthiessen's rule is found to decrease with cold work, while the residual resistivity increases. The lattice imperfections also have strong effects on the thermoelectric power. A critical discussion focuses on the relation of and discrimination among these effects.
Similar content being viewed by others
References
A. D. Caplin and C. Rizzuto,J. Phys. C 3, L117 (1970).
M. R. Cimberle, G. Bobel, and C. Rizzuto,Adv. Phys. 23, 639 (1974).
J. Bass,Adv. Phys. 21, 431 (1972).
Yu Kagan and A. P. Zhernov,Sov. Phys.—JETP 33, 990 (1971).
W. E. Lawrence and J. W. Wilkins,Phys. Rev. B 6, 4466 (1972).
J. W. Ekin and A. Bringer,Phys. Rev. B 7, 4468 (1973).
Y. Bergman, M. Kaveh, and N. Wiser,Phys. Rev. Lett. 32, 606 (1974).
I. A. Cambell, A. D. Caplin, and C. Rizzuto,Phys. Rev. Lett. 26, 239 (1971).
L. Dworin,Phys. Rev. Lett. 26, 1244 (1971).
A. D. Caplin, F. Napoli, and D. Sherrington,J. Phys. F 3, L93 (1973).
R. Krsnik, E. Babic, and C. Rizzuto,Solid State Comm. 12, S91 (1973).
S. Senoussi and I. A. Campbell,J. Phys. F 3, L102 (1973).
A. R. De Vroomen, C. Van Baarle, and A. J. Cuelenaere,Physica 26, 19 (1960).
R. S. Averback, C. H. Stephan, and J. Bass,J. Low Temp. Phys. 12, 319 (1973).
T. Fujita and T. Ohtsuka,Japan. J. Appl. Phys. 15, 881 (1976).
J. C. Garland and R. Bowers,Phys. Kondens. Materie 9, 36 (1969).
E. W. Fenton, J. S. Rogers, and S. B. Woods,Can. J. Phys. 41, 2026 (1963).
J. A. Rowlands and S. B. Woods,J. Phys. F 5, L100 (1975).
L. Nordheim and C. J. Gorter,Physica 2, 383 (1935).
R. P. Huebener,Phys. Rev. 171, 634 (1968).
P. E. Nielsen and P. L. Taylor,Phys. Rev. B 10, 4061 (1974).
F. Napoli and D. Sherrington,J. Phys. F 1, L53 (1971).
W. B. Willott,Phil. Mag. 16, 691 (1961).
K. Kawamura, preprint.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Fujita, T., Ohtsuka, T. Transport properties of cold-worked aluminum at low temperatures. J Low Temp Phys 29, 333–344 (1977). https://doi.org/10.1007/BF00655098
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF00655098